PEMBUATAN LAPISAN TIPIS TiO2 BERBASIS ILMENIT LAMPUNG MENGGUNAKAN METODE CHEMICAL BATH DEPOSITION (CBD)

NADIA FEBRIYANTI, 1717041008 (2021) PEMBUATAN LAPISAN TIPIS TiO2 BERBASIS ILMENIT LAMPUNG MENGGUNAKAN METODE CHEMICAL BATH DEPOSITION (CBD). Fakultas Teknik, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK - ALLIF Printing (1).pdf Download (262Kb) | Preview
	File PDF 2. SKRIPSI FULL - ALLIF Printing (1).pdf Restricted to Hanya staf Download (2685Kb)
Preview	File PDF 3. SKRIPSI FULL TANPA BAB PEMBAHASAN - ALLIF Printing (1).pdf Download (2669Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian pembuatan lapisan tipis TiO2 berbasis ilmenit Lampung dengan menggunakan metode Chemical Bath Deposition (CBD). Prekursor yang digunakan dalam pembuatan lapisan tipis TiO2 pada penelitian ini berupa serbuk hasil ekstraksi TiO2 dari ilmenit Lampung dengan kemurnian sebesar 60,701%. Lapisan tipis TiO2 ditumbuhkan pada media berupa substrat kaca. Variasi yang digunakan dalam penumbuhan lapisan tipis pada penelitian ini berupa waktu pelapisan yaitu 2, 3, 4 dan 5 jam. Setelah proses pelapisan, substrat kaca dikeringkan dan dikalsinasi pada suhu 500C selama 4 jam. Kemudian dilakukan karakterisasi menggunakan XRD dan SEM, serta dilakukan pengukuran nilai resistivitas dari lapisan tipis dengan menggunakan metode empat titik. Hasil XRD menunjukkan bahwa serbuk hasil ekstraksi TiO2 dari ilmenit Lampung didominasi oleh fasa rutil dan brukit. Sedangkan untuk lapisan tipis TiO2 yang dihasilkan berstruktur amorf. Morfologi pada semua sampel menunjukkan bahwa telah terbentuk struktur berpori. Berdasarkan hasil SEM penampang melintang, pada sampel dengan waktu pelapisan 3 jam memiliki ketebalan lapisan sebesar 7,28 μm. Berdasarkan pengukuran resistivitas didapatkan hasil bahwa semakin lama waktu pelapisan maka semakin besar nilai resistivitas rata-ratanya. Kata Kunci: Chemical Bath Deposition, ilmenit, lapisan tipis, TiO2 Research has been carried out on the fabrication of thin film TiO2 based on ilmenite in Lampung using the chemical bath deposition (CBD) method. The precursor used in the manufacture of TiO2 thin films in this study was a powder extracted from TiO2 from Lampung ilmenite with a purity of 60.701%. A thin layer of TiO2 was grown on a medium in the form of a glass substrate. The variation used in the growth of the thin layer in this study were 2, 3, 4, and 5 hours coating time. After the coating process, the glass substrate was dried and calcined at 500 C for 4 hours. Then the characterization was carried out using XRD, SEM and the resistivity value of the thin layer was measured using the four-point method. The XRD results showed that the TiO2 powder extracted from Lampung ilmenite was dominated by the rutile and brookite phases. As for the resulting thin layer of TiO2, the structure is amorphous. The morphology of all samples showed that a porous structure had been formed. Based on the cross-sectional SEM results, the sample with a coating time of 3 hours had a layer thickness of 7,28 μm. Based on the resistivity measurement, it was found that the longer the coating time, the greater the average resistivity value. Keywords: chemical bath deposition, ilmenite, thin film, TiO2.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Dito Nipati
Date Deposited:	27 Apr 2022 02:15
Terakhir diubah:	27 Apr 2022 02:15
URI:	http://digilib.unila.ac.id/id/eprint/60551

Actions (login required)

Lihat Karya Akhir