PENGARUH VARIASI KOMPOSISI BIJIH BESI DENGAN BATU SPLIT TERHADAP SIFAT FISIS DAN MEKANIS BETON K. 350 DENGAN UMUR PERENDAMAN 7, 14, DAN 28 HARI

Afrizal Halim, 1617041098 (2021) PENGARUH VARIASI KOMPOSISI BIJIH BESI DENGAN BATU SPLIT TERHADAP SIFAT FISIS DAN MEKANIS BETON K. 350 DENGAN UMUR PERENDAMAN 7, 14, DAN 28 HARI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF 1617041098-Afrizal Halim-Abstrak - Afrizal Halim.pdf Download (85Kb) | Preview
	File PDF 1617041098-Afrizal Halim-Skripsi Full - Afrizal Halim.pdf Restricted to Hanya staf Download (2078Kb)
Preview	File PDF 1617041098-Afrizal Halim-Skripsi Tanpa Pembahasan - Afrizal Halim.pdf Download (2080Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian beton K.350 menggunakan variasi bijih besi dengan batu split sebagai komposisi pembuatan beton K.350 dengan umur perendaman 7, 14 dan 28 hari yang menggunakan metode hidrolisis. Bahan-bahan yang digunakan dalam penelitian ini yaitu bijih besi, batu split, pasir, air dan semen. Variasi komposisi bijih besi dan batu split adalah 0:100 Wt%, 10:90 Wt%, 20:80 Wt%, 30:70 Wt%, 40:60 Wt% dan 50:50 Wt%. Pada sampel terlihat bahwa konsentrasi bijih besi berpengaruh terhadap nilai kuat tekan, porositas, absorpsi, pembentukan fasa dan konsentrasi senyawa kimia pada beton K.350. Nilai kuat tekan terbaik terdapat pada variasi komposisi 50:50 Wt% dengan umur perendaman 28 hari sebesar 43,77 MPa. Nilai porositas dan absorpsi terbaik terdapat pada variasi komposisi 50:50 Wt% dengan umur perendaman 28 hari sebesar 4,02 % dan 1,63 %. Perubahan juga terjadi pada intensitas fasa hematite dan konsentrasi senyawa Fe2O3 seiring dengan bertambahnya konsentrasi bijih besi. Kata Kunci: Beton K.350, Bijih Besi, Absorpsi, Porositas. ii K.350 concrete research uses iron ore variation with split stone as the composition of K.350 concrete making with immersion life of 7, 14 and 28 days using hydrolysis method. The materials used in this study are iron ore, split stone, sand, water and cement. Variations in the composition of iron ore and split stone are 0:100 Wt%, 10:90 Wt%, 20:80 Wt%, 30:70 Wt%, 40:60 Wt% and 50:50 Wt%. In the sample it is seen that the concentration of iron ore affects the strong value of press, porosity, absorption, phase formation and concentration of chemical compounds in concrete K.350. The best press strength value is found in the composition variation of 50:50 Wt% with a 28-day immersion life of 43.77 MPa. The best porosity and absorption values are found in the composition variation of 50:50 Wt% with a 28-day immersion life of 4.02 % and 1.63 %. Changes also occur in the intensity of the hematite phase and the concentration of Fe2O3 compounds in line with the increasing concentration of iron ore. Kata Kunci: K.350 Concrete, Iron Ore, Absorption, Porosity.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	28 Apr 2022 07:23
Terakhir diubah:	28 Apr 2022 07:23
URI:	http://digilib.unila.ac.id/id/eprint/60646

Actions (login required)

Lihat Karya Akhir