PENGARUH PERLAKUAN ASAM NITRAT PADA PERMUKAAN PARTIKEL CARBON NANOTUBE (CNT) TERHADAP KEKUATAN TARIK KOMPOSIT HYBRID CARBON FIBER/CNT/EPOXY

Ahmad Farid Akram, 1515021044 (2021) PENGARUH PERLAKUAN ASAM NITRAT PADA PERMUKAAN PARTIKEL CARBON NANOTUBE (CNT) TERHADAP KEKUATAN TARIK KOMPOSIT HYBRID CARBON FIBER/CNT/EPOXY. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
1. ABSTRAK - ABSTRACT - AHMAD FARID AKRAM.pdf

Download (13Kb) | Preview
[img] File PDF
2. SKRIPSI FULL - AHMAD FARID AKRAM.pdf
Restricted to Hanya staf

Download (3542Kb)
[img]
Preview
File PDF
3. SKRIPSI FULL TANPA PEMBAHASAN - AHMAD FARID AKRAM.pdf

Download (1799Kb) | Preview

Abstrak

Komposit ialah suatu material yang terbentuk oleh campuran dari dua atau lebih material pembentuknya. Carbon nanotube digunakan sebagai penguat filler komposit yang dapat menambah kekuatan tarik komposit tersebut. Namun carbon nanotube yang didapat dari produsen terdapat pengotor yang dapat mengurangi adhesi pada matriks yang digunakan. Penelitian kali ini bertujuan untuk mengetahui pengaruh perlakuan permukaan partikel carbon nanotube (CNT) dengan menggunakan asam nitrat terhadap kekuatan tarik komposit hybrid carbon fiber/CNT/epoxy. Komposit terbentuk dari pencampuran carbon fiber, serbuk penguat filler carbon nanotube, dan matriks polimer epoxy. Serbuk penguat carbon nanotube dilakukan perlakuan permukaan menggunakan asam nitrat dengan kadar 1 M, 3 M, dan 5 M selama 15 menit diatas hot plate magnetic stirer. Setelah itu dicuci menggunakan hidrogen peroksida 30% selama 15 menit, lalu dibersihkan dengan aquades dan dikeringkan. Komposit dilakukan fabrikasi dengan fraksi massa 0.5% CNT, 20% carbon nanotube, dan 79.5% epoxy dengan metode vacuum bagging. Untuk mengetahui sifat mekanik dari komposit hybrid carbon fiber/CNT/epoxy dilakukan pengujian tarik dengan menggunakan standar ASTM D638-03. Selain itu dilakukan pengamatan scanning electron microscope untuk mengetahui mekanisme kegagalan komposit hybrid carbon fiber/CNT/epoxy. Hasil pengujian tarik dengan menggunakan standar ASTM D638-03 komposit hybrid carbon fiber/CNT/epox. Komposit tertinggi yaitu carbon fiber/CNT dengan perlakuan asam nitrat 1 M mempunyai nilai tegangan tarik sebesar 42.23 MPa, nilai regangan sebesar 17.84 % dan nilai modulus elastisitas sebesar 0.2368 GPa. Pada hasil pengamatan menggunakan scanning electron microscope campuran epoxy dengan CNT yang telah dilakukan perlakuan permukaan menggunakan asam nitrat 1 M memperlihatkan adhesi yang lebih baik dibandingkan dengan perlakuan asam nitrat 3 M dan 5 M. _________ Kata kunci : komposit, carbon nanotube, asam nitrat, uji tarik, scanning electron microscope. Composite is a material formed by a mixture of two or more constituent materials. Carbon nanotubes are used as reinforcement for fillers composite which can increase the tensile strength of the composite. However, carbon nanotubes obtained from manufacturers contain impurities that can reduce adhesion to the matrix used. This study aims to determine the effect of surface treatment of particles carbon nanotube (CNT) using nitric acid on the tensile strength of composites hybrid carbon fiber/CNT/epoxy. Composites are formed by mixing carbon fiber,reinforcing powder carbon nanotube filler, and a polymer matrix epoxy. The Reinforcing powder was carbon nanotube surface treated using nitric acid with levels of 1 M, 3 M, and 5 M for 15 minutes on a hot plate magnetic stirrer. After that, it was washed using 30% hydrogen peroxide for 15 minutes, then cleaned with distilled water and dried. Composites were fabricated with a mass fraction of 0.5% CNT, 20% carbon nanotubes, and 79.5% epoxy using the method vacuum bagging. To determine the mechanical properties of composites hybrid carbon fiber/CNT/epoxy tensile tests were carried out using the ASTM D638-03 standard. In addition, observations were made scanning electron microscope to determine the failure mechanism of the composite carbon fiber/CNT/epoxy hybrid. Tensile test results using ASTM D638-03 standard composite hybrid carbon fiber/CNT/epoxy. The highest composite, namely carbon fiber/CNT with 1 M nitric acid treatment, had a tensile stress value of 42.23 MPa, a strain value of 17.84 % and a modulus of elasticity of 0.2368 GPa. In observations using a scanning electron microscope, a mixture of epoxy and CNT that had been surface treated using 1 M nitric acid showed better adhesion than 3 M and 5 M nitric acid treatment. _________ Key words: composite, carbon nanotube, nitric acid, test pull, scanning electron microscope.

Jenis Karya Akhir: Skripsi
Subyek: 600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi: Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit: UPT . Meda Sulistiana
Date Deposited: 27 May 2022 03:27
Terakhir diubah: 27 May 2022 03:27
URI: http://digilib.unila.ac.id/id/eprint/61844

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir