PENGARUH VARIASI WAKTU PACK CARBURIZING ARANG TEMPURUNG KELAPA PADA BAJA ST37 DENGAN KATALIS CANGKANG KERANG HIJAU

TOMMY RIZKY PUTRA PERDANA, 1515021051 (2021) PENGARUH VARIASI WAKTU PACK CARBURIZING ARANG TEMPURUNG KELAPA PADA BAJA ST37 DENGAN KATALIS CANGKANG KERANG HIJAU. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK - ABSTRACT - Rocket Digital (20).pdf Download (34Kb) | Preview
	File PDF 2. SKRIPSI FULL - Rocket Digital (55).pdf Restricted to Hanya staf Download (1410Kb)
Preview	File PDF 3. SKRIPSI TANPA BAB PEMBAHASAN - Rocket Digital (55).pdf Download (1376Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini bertujuan untuk mengetahui pengaruh arang tempurung kelapa dalam proses carburizing baja karbon ST37 terhadap kekerasan, komposisi kimia dan struktur mikronya. Temperatur yang digunakan dalam proses karburasi berlangsung adalah 850oC dengan waktu tahan 60, 120 dan 180 menit. Baja karbon ST37 yang mengandung kadar C = 0,0372 %, Si = 0,40 %, Mn = 0,105 %, P = 0,0378 %, S = 0,028 % dan Fe = 93,8 %. Hasil pengujian kekerasan micro vickers dengan nilai tertinggi sebesar 218,49 HV pada waktu penahanan 60 menit menggunakan arang kayu jati dan sengon sebesar 224 HV. Hasil analisis uji komposisi kimia pada arang tempurung kelapa pada waktu penahanan 60 menit 0,241 %, 120 menit 0,375 %, dan 180 menit 0,323 %, data ini menunjukkan bahwa nilai kekerasan spesimen pengaruh arang tempurung kelapa lebih tinggi pada proses carburizing di waktu penahanan 120 menit sehingga jumlah karbon mampu berdifusi dipermukaan baja karbon tersebut. Kata kunci: kekerasan, komposisi kimia, arang tempurung kelapa, baja karbon ST37 dan karburasi. This research is aimed to know the influence of coconut shell charcoal in the low carburizing process of ST37 towards the endurance and to know the effect of carburizing process on the chemical composition and microstructure of low carbon steel ST37. The temperature used in the carburizing procces id 850oC with holding time of 60 , 120, and 180 minutes. Low carbon steel ST37 which contains of C = 0.0372%, Si = 0.40%, Mn = 0.105%, P = 0.0378%, S = 0.028% and Fe = 93.8%. The results of micro vickers hardness test with the highest value of 218,49 HV at 60 minutes of holding time using coconut shell charcoal of 218,49 HV. The analysis of the chemical composition of coconut shell charcoal 0.241% at 60 minutes of holding time,120 minutes is 0,375%, and 180 is 0,323%. this data shows that the hardness value of specimens influences coconut shell charcoal is higher in the carburizing process at 120 minutes holding time, so that the amount of carbon is able to diffuse on the surface of carbon steel. Key words: hardness, chemical compositon coconut shell charcoal, low carbon steel ST37 and carburizing

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Meda Sulistiana
Date Deposited:	30 May 2022 04:29
Terakhir diubah:	30 May 2022 04:29
URI:	http://digilib.unila.ac.id/id/eprint/62092

Actions (login required)

Lihat Karya Akhir