STUDI PENGARUH PERLAKUAN KIMIA SERAT SABUT KELAPA TERHADAP KEKUATAN TARIK KOMPOSIT SERAT SABUT KELAPA/KARET ALAM

AYOGA TRI ISMI AJI, 1515021002 (2021) STUDI PENGARUH PERLAKUAN KIMIA SERAT SABUT KELAPA TERHADAP KEKUATAN TARIK KOMPOSIT SERAT SABUT KELAPA/KARET ALAM. Fakultas Teknik, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK-ABSTRACT - Finta Yaya (3).pdf Download (6Mb) | Preview
	File PDF 2. SKRIPSI FULL - Finta Yaya (5).pdf Restricted to Hanya staf Download (6Mb)
Preview	File PDF 3. SKRIPSI TANPA BAB PEMBAHASAN - Finta Yaya (4).pdf Download (6Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Komposit merupakan penggabungan dua material atau lebih yang memiliki sifat material yang berbeda. Karet alam merupakan salah satu material terbaharukan yang dapat digunakan dalam pembuatan komposit. Penelitian ini bertujuan untuk mengetahui pengaruh perakuan kimia serat sabut kelapa terhadap kekuatan tarik komposit serat sabut kelapa dan karet alam. Dalam penelitian ini menggunakan perlakuan kimia NaOH sebesar 5% dan asetet anhidrida dengan perlakuan kimia asetat anhidrida 5%, 10% dan 15%. Proses pembuatan komposit yang pertama yaitu karet alam dan asam formiat dituangan kedalam cetakan. Kemudian komposit di pres dan proses selanjutnya komposit di oven. Pengujian yang dilakukan adalah pengujian tarik yang menghasilkan nilai rata-rata kekuatan tarik tertinggi pada komposit karet alam- serat sabut kelapa perlakuan kimia 10% sebesar 4.684 MPa dan nilai rata-rata kekuatan tarik terendah pada komposit karet alam-serat sabut kelapa pelakuan kimia 5% sebesar 3.033 MPa. Tingkat kadar perlakuan kimia asetat anhidrida pada serat mempengaruhi kekuatan tarik yang dihasilkan serta ikatan antarmuka yang terbentuk seperti pada pengamatan foto SEM. Pada pengamatan foto SEM dapat dilihat ikatan antar muka dan adhesi antara serat sabut kelapa dan karet alam meningkat. Kata kunci: Komposit, Naoh, Asetat Anhidrida, Karet Alam, Serat Alam, Uji Tarik, SEM. Composite is a combination of two or more materials that have different material properties. Natural rubber is one of the renewable materials that can be used in the manufacture of composites. The purpose of this research to determine the effect of chemical treatment of coco fiber on the tensile strength of composites of coconut coir fiber and natural rubber. In this study, the chemical treatment of 5% NaOH and acetic anhydride with chemical treatment variants of 5%, 10% and 15% chemical treatment of acetic anhydride was used. The first composite manufacturing process is natural rubber and formic acid then pouring it into the mold. After that, the specimen press and oven. The test carried out is a tensile test which produces the highest average value of tensile strength in the natural rubber-coconut shabu fiber composite chemical treatment 10% of 4. 684 MPa and the average value of the lowest tensile strength in the natural rubber-coconut fiber composite using 5% chemical treatment was 3,033 MPa. The level of chemical treatment of acetic anhydride on the fiber affects the tensile strength produced and the interfacial bond formed as seen in the SEM photo observations. In the SEM photo observation, it can be seen that the interfacial bond and the adhesion between coconut coir fiber and natural rubber increased. . Keywords: Composite, , NaOH, Acetic Anhydride, Natural Rubber, Natural Fiber, TensileTest, SEM.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) 600 Teknologi (ilmu terapan) > 630 Pertanian dan teknologi yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Dito Nipati
Date Deposited:	31 May 2022 02:32
Terakhir diubah:	31 May 2022 02:32
URI:	http://digilib.unila.ac.id/id/eprint/62213

Actions (login required)

Lihat Karya Akhir