ANALISIS EFEKTIVITAS CAMPURAN METIL ESTER TURUNAN MINYAK BIJI KARET (Hevea brasiliensis) DENGAN DIETANOLAMINA SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2)

NIKITA DAMAYANTI, 1757011004 (2021) ANALISIS EFEKTIVITAS CAMPURAN METIL ESTER TURUNAN MINYAK BIJI KARET (Hevea brasiliensis) DENGAN DIETANOLAMINA SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Nikita Damayanti.pdf Download (2471Kb) | Preview
	File PDF SKRIPSI FULL - Nikita Damayanti.pdf Restricted to Hanya staf Download (2945Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN - Nikita Damayanti.pdf Download (2945Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk menguji efektivitas campuran dietanolamina dan metil ester turunan minyak biji karet sebagai inhibitor korosi baja lunak dalam medium larutan garam yang mengandung CO2. Metil ester dibuat dengan transesterifikasi minyak biji karet menggunakan metanol dengan katalis zeolit-A. Serangkaian campuran dibuat dengan mencampur dietanolamina dan metil ester dengan perbandingan 0:5; 1:4; 2:3; 3:2; 4:1; dan 5:0. Percobaan inhibitor korosi dilakukan dalam larutan NaCl 3% jenuh dengan CO2 menggunakan metode wheel test dan morfologi atau sampel permukaan logam dianalisis menggunakan SEM. Hasil yang diperoleh menunjukkan bahwa persentase proteksi tertinggi sebesar 60,11% diperoleh dari percobaan menggunakan larutan inhibitor dengan perbandingan dietanolamina terhadap metil ester 3:2. Proteksi inhibitor juga ditunjukkan oleh morfologi permukaan sampel yang dilihat dengan SEM. Kata Kunci : Inhibitor korosi, baja lunak, metil ester, minyak biji karet, wheel test. This research was conducted to study the ability of mixed diethanolamine and rubber seed oil-derived methyl esters as corrosion inhibitor of mild steel in CO2 containing brine solution. Methyl esters were prepared by transesterification of rubber seed oil using methanol in the presence of zeolite-A as catalyst. A series of mixtures were prepared by mixing methyl esters and diethanolamine with the ratios of 5:0; 4:1; 3:2; 2:3; 1:4; and 0:5. Corrosion inhibition experiments were conducted in a 3% NaCl solution saturated with CO2 using wheel test method, and the morphology of the metal sample was analyzed using Scanning Electron Microscope (SEM). The results obtained indicate that the highest percent of protection of 60.11% was obtained from the experiment using the inhibitor solution with the ratio of methyl esters to diethanolamin to of 3:2. The protection of the inhibitor was also indicated by surface morphology of the sample as seen by SEM. Keywords: Corrosion inhibitor, mild steel, rubber seed oil methyl ester, wheel test.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	AM.d Firlia Hidayah
Date Deposited:	09 Aug 2022 07:50
Terakhir diubah:	09 Aug 2022 07:50
URI:	http://digilib.unila.ac.id/id/eprint/64691

Actions (login required)

Lihat Karya Akhir