EFEK TERMAL HARDENING DENGAN PERLAKUAN PANAS SIKLIK TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS BAJA TAHAN KARAT 316

KMS. IMAM PRAWIJAYA, 1815021024 (2022) EFEK TERMAL HARDENING DENGAN PERLAKUAN PANAS SIKLIK TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS BAJA TAHAN KARAT 316. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (3198Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3199Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3201Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK EFEK TERMAL HARDENING DENGAN PERLAKUAN PANAS SIKLIK TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS BAJA TAHAN KARAT 316 Oleh Kms. Imam Prawijaya Baja tahan karat tipe 316 memiliki nilai kekerasan yang rendah sehingga pengaplikasiannya sangat dibatasi. Berdasarkan penelitian yang telah dilakukan sebelumnya, perlakuan panas siklus banyak memiliki dampak positif terhadap sifat mekanis dari material uji. Perlakuan panas siklus membuat struktur butir menjadi semakin halus, meningkatkan nilai ketangguhan dan kekerasan. Metode perlakuan panas siklus adalah sebagai berikut: pertama, untuk menentukan optimal siklus dilakukan pengujian siklus pada temperature 950℃ dan waktu tahan 3,3 menit dengan jumlah 3,5 dan 7 kali siklus dan diquenching pada media air. Setelah dilakukan pengujian siklus optimal dilakukan perlakuan panas siklus pada siklus optimal dengan waktu tahan 40 menit dan pada tiga variasi temperatur yaitu 550, 750 dan 950℃ dengan metode carburizing dan diquenching pada media es. Untuk melihat pengaruh pada sifat mekanis dilakukan pengujian kekerasan microhardness Vickers, untuk karakterisasi dalam menentukan sifat kimia dan fisik dilakukan uji XRF, XRD, SEM-EDS dan mikroskop optik. Berdasarkan pengujian kekerasan, nilai kekerasan menurun seiring dengan peningkatan temperatur. Pada pengujian XRF, komposisi unsur krom 16% yang berarti bahwa sampel merupakan baja tahan karat 316, Berdasarkan pengujian SEM-EDS dan mikroskop optik didapati terbentuk lapisan pada material yang diberikan perlakuan carburizing, ketebalan lapisan yang terbentuk meningkat seiring peningkatan temperatur dan intensitas karbon tertinggi pada bagian permukaan sampel. Pada pengujian XRD sampel yang diberikan perlakuan pada temperatur 750 dan 950℃ terbentuk fasa kromium oksida (Cr2O3) dan besi oksida (Fe3O4) sedangkan pada sampel 550℃ didominasi oleh fasa ferit dan ferit nikel tetragonal. Kata Kunci: Baja tahan karat tipe 316, perlakuan panas siklus, carburizing ABSTRAK THERMAL EFFECTS OF HARDENING WITH CYCLIC HEAT TREATMENT ON MICRO STRUCTURE AND MECHANICAL PROPERTIES OF STEEL 316 By Kms. Imam Prawijaya Type 316 stainless steel has a low hardness value so its application is very limited. Based on previously conducted studies, cycle heat treatment has a lot of positive impact on the mechanical properties of the test material. Cyclical heat treatment makes the grain structure even more refined, increasing the value of toughness and hardness. The method of heat treatment of the cycle is as follows: first, to determine the optimal cycle, cycle testing is carried out at a temperature of 950 ° C and a resistance time of 3.3 minutes with an amount of 3.5 and 7 cycles and quenching on water media. After testing the optimal cycle, cycle heat treatment was carried out in the optimal cycle with a lasting time of 40 minutes and at three temperature variations of 550, 750 and 950 ° C by the method of carburizing and quenching on ice media. To see the influence on mechanical properties, Vickers microhardness hardness testing was carried out, for characterization in determining chemical and physical properties, XRF, XRD, SEM-EDS and optical microscope tests were carried out. Based on hardness testing, the hardness value decreases as the temperature increases. In the XRF test, the elemental composition of chrome was 16% which means that the sample was stainless steel 316, Based on SEM-EDS testing and optical microscopy, it was found that a layer was formed on the material given the carburizing treatment, the thickness of the formed layer increases as the temperature and intensity of the highest carbon increase on the surface of the sample. In XRD testing, samples treated at temperatures 750 and 950 °C formed phases of chromium oxide (Cr2O3) and iron oxide (Fe3O4) while in samples 550 °C were dominated by ferrite phase and tetragonal nickel ferrite. Keywords: Type 316 stainless steel, cycle heat treatment, carburizing

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	2208420187 . Digilib
Date Deposited:	23 Aug 2022 01:40
Terakhir diubah:	23 Aug 2022 01:40
URI:	http://digilib.unila.ac.id/id/eprint/65407

Actions (login required)

Lihat Karya Akhir