ANALISIS VARIASI BAHAN PEREKAT DAN TEKANAN PADA BATA RINGAN BERBAHAN DASAR PERLIT DAN BASALT

Prinanti, 1517041104 (2022) ANALISIS VARIASI BAHAN PEREKAT DAN TEKANAN PADA BATA RINGAN BERBAHAN DASAR PERLIT DAN BASALT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF (ABSTRAK)
ABSTRAK.pdf

Download (15Kb) | Preview
[img] File PDF (SKRIPSI FULL)
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (2712Kb) | Minta salinan
[img]
Preview
File PDF (SKRIPSI FULL TANPA BAB PEMBAHASAN)
SKRIPSI TANPA BAB PEMBAHASAN..pdf

Download (584Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Penelitian ini telah dilakukan untuk menganalisa pengaruh bahan perekat dan tekanan terhadap sifat fisis bata ringan berbahan dasar perlit dan basalt, mengetahui komposisi paling optimum dari bahan perekat dan tekanan yang digunakan, serta untuk mengetahui senyawa oksida dan struktur fasa perlit sebelum dan setelah terbentuk bata ringan. Dalam penelitian ini, expanded perlite digunakan sebagai bahan utama bata ringan; basalt sebagai filler; kaolin, semen putih, dan bentonit sebagai bahan perekat. Penambahan basalt dan bahan perekat untuk meningkatkan mutu bata ringan. Hasil yang diperoleh menunjukkan bahwa tekanan tidak mempengaruhi komposisi kimia dan fasa bata ringan namun berpengaruh pada sifat fisisnya. Densitas terendah sebesar 1,353 g/cm3dimiliki sampel bata ringan dengan perekat semen putih dengan tekanan pencetakan 1 ton. Kuat tekan optimum dan absorbsi minimum dimiliki bata ringan dengan perekat bentonit yaitu sebesar 2,222 MPa dan 2,778% pada tekanan pencetakan 1 ton dan 2 ton. Porositas tertinggi sebesar 52,941% terjadi pada bata ringan dengan perekat semen putih tekanan pencetakan 1 ton. Hasil analisis XRF menunjukkan konsentrasi SiO2, Fe2O3, Al2O3, dan CaO bahan campuran bahan bata ringan cenderung lebih tinggi dibandingkan setelah terbentuk bata ringan. Hasil analisis XRD pada bahan pembentuk bata ringan menunjukkan fasa anorthite dan hematite adalah fasa yang paling dominan, hanya saja pada XRD untuk produk bata ringan jumlahnya lebih sedikit. Fasa lain yang muncul pada bata ringan yaitu, cristobalite, muscovite, ternesite dan diopside. Kata Kunci : bata ringan, expanded perlite, densitas, kuat tekan, porositas, absorbsi. ABSTRACT This research was carried out to analyze the effect of adhesive and pressure on the physical properties of lightweight brick made of perlite and basalt, to determine the optimum composition of the adhesive and the used pressure, as well as to determine the oxide compound and the structure of the perlite phase before and after the lightweight brick was formed. In this research, expanded perlite was used as the main material for lightweight bricks; basalt as a filler; kaolin, white cement and bentonite as an adhesive. The addition of basalt and adhesives to improve the quality of lightweight bricks. The results indicate that the pressure does not affect the chemical composition and phase of the lightweight brick but does affect its physical properties. The lowest density of 1.353 g/cm3 was obtained from a lightweight brick sample with white cement adhesive which was pressured 1 ton. The optimum compressive strength and minimum absorption of lightweight brick with bentonite adhesive are 2.222 MPa and 2.778% respectively at a pressure of 1 ton and 2 tons. The highest porosity of 52.941% occurred in lightweight bricks with a pressure of 1 ton of white cement adhesive. The results of XRF analysis show that the concentration of SiO2, Fe2O3, Al2O3, and CaO in by dough of lightweight bricks tends to be higher than the lightweight bricks. The results of XRD analysis of the rough material show that anorthite and hematite are the most dominant phases, which is fewer than in the lightweight brick products. Other phases that appear in lightweight bricks are cristobalite, muscovite, ternesite and diopside. Keywords : lightweight brick, expanded perlite, density, compressive strength, porosity, absorption.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: 2208422234 . Digilib
Date Deposited: 23 Aug 2022 08:30
Terakhir diubah: 23 Aug 2022 08:30
URI: http://digilib.unila.ac.id/id/eprint/65469

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir