PENGARUH PENGUAT SERAT PADA SIFAT TARIK KOMPOSIT PLA/OPEFB (OIL PALM EMPTY FRUIT BUNCH) UNTUK APLIKASI BIODEGRADABLE TENDON SCAFFOLD

ADI SAPUTRA, RIZAL (2022) PENGARUH PENGUAT SERAT PADA SIFAT TARIK KOMPOSIT PLA/OPEFB (OIL PALM EMPTY FRUIT BUNCH) UNTUK APLIKASI BIODEGRADABLE TENDON SCAFFOLD. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF (ABSTRAK) ABSTRAK (ABSTRACT).pdf Download (3187Kb) | Preview
	File PDF (TESIS FULL) TESIS FULL.pdf Restricted to Hanya staf Download (3643Kb) | Minta salinan
Preview	File PDF (TESIS TANPA BAB PEMBAHASAN) TESIS TANPA BAB PEMBAHASAN.pdf Download (3626Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Perkebunan kelapa sawit di Indonesia terus mengalami peningkatan setiap tahunnya. Pada pengolahan 1 ton TBS (Tandan Buah Segar) menghasilkan TKKS sebanyak 22–23% (220–230 kg). Serat TKKS dapat dimanfaatkan sebagai serat alami reinforcement komposit untuk aplikasi biomedis (Biomaterial). Poly Lactic acid (PLA) telah banyak digunakan sebagai material biomedis karena sifat biodegradable dan biocompatible nya sebagai scaffold. Scaffold berfungsi untuk merangsang, tumbuh, dan membimbing regenerasi sel dan jaringan baru, yang dapat ter-degradasi secara klinis dan biomekanik. Kerusakan pada tendon/ligamen sering terjadi akibat beban yang berlebihan sehingga diperlukan scaffold biodegradable dari PLA untuk memperbaikinya. Namun PLA memiliki sifat mekanik yang lebih rendah dari tendon/ligamen sehingga diperlukan reinforcement berupa serat alam yang tidak berbahaya. Sebelum digunakan serat TKKS treatment menggunakan larutan alkali NaOH 5%/3 jam dan microwave oven 100oC/15 menit. Selanjutnya komposit PLA/TKKS dibentuk dengan metode hand lay-up dengan jenis serat tunggal dan serat braids dengan fraksi volume serat 25%. Serat braids di sesuaikan agar mirip dengan serat dari tendon/ligamen. Serat TKKS di analisis kadar air dan sifat kimia, kemudian komposit PLA/TKKS diuji tarik, uji bending, analisis SEM, dan perhitungan analitik ROM (Rule Of Mixture). Hasil dari pengujian mekanik menggunakan serat tunggal dan serat braids dapat meningkatkan sifat mekanik dari PLA sehingga dapat digunakan sebagai scaffold tendon/ligament biodegradable. Kata kunci : Serat TKKS, Serat braids, PLA, Sifat mekanik, Tendon scaffold. Oil palm processing in Indonesia has increased every year. Processing 1 ton of FFB (Fresh Fruit Bunches) produces 22–23% (220–230 kg) OPEFB. OPEFB fiber can be used as a natural fiber composite reinforcement for biomedical applications (biomaterials). Poly Lactic acid (PLA) has been used as a biomedical material because biodegradable and biocompatible properties scaffold. Scaffold functions to stimulate, grow, and guide the regeneration of new cells and tissue engineering, can be degraded clinically and biomechanically. Fracture tendons/ligaments effect overload, so needed a biodegradable scaffold from PLA to repair it. However, PLA has lower mechanical properties than tendons/ligaments so needed reinforcement form natural fibers non toxic. Before use, the OPEFB fiber was treated using 5% NaOH solution for 3 hours and a microwave oven at 100oC/15 minutes. Furthermore, PLA/TKKS composite was produced hand lay-up method with a single continuous fiber and braids fiber with fiber volume fraction 25%. The fibers of the braids are adjusted to same the fibers of the tendons/ligaments. OPEFB fiber was analyzed for moisture content and chemical properties, and then PLA/TKKS composite characterization tensile properties, bending test, SEM analysis, and analytical calculation of ROM (Rule Of Mixture). The results of mechanical testing using single fibers and braids can improve the mechanical properties of PLA so can be used as a biodegradable tendon/ligament scaffold. Keywords : OPEFB fiber, Braids fiber, PLA, Mechanical properties, Scaffold tendon.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi Magister Teknik Mesin
Pengguna Deposit:	2208612077 . Digilib
Date Deposited:	12 Dec 2022 04:19
Terakhir diubah:	12 Dec 2022 04:19
URI:	http://digilib.unila.ac.id/id/eprint/67471

Actions (login required)

Lihat Karya Akhir