UJI STABILITAS DAN KEMAMPUAN KOPOLI (EUGENOL-DIALIL FTALAT) 8% SEBAGAI CARRIER PADA TRANSPOR FENOL MENGGUNAKAN METODE PIM (POLYMER INCLUSION MEMBRANE)

Dela Ananda Putri, 1717011045 (2021) UJI STABILITAS DAN KEMAMPUAN KOPOLI (EUGENOL-DIALIL FTALAT) 8% SEBAGAI CARRIER PADA TRANSPOR FENOL MENGGUNAKAN METODE PIM (POLYMER INCLUSION MEMBRANE). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK - Dela Ananda.pdf

Download (1995Kb) | Preview
[img] File PDF
SKRIPSI FULL - Dela Ananda.pdf
Restricted to Hanya staf

Download (2562Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN - Dela Ananda.pdf

Download (2562Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Studi stabilitas dan kemampuan transpor fenol menggunakan Copoli-Eugenol Dialil Ftalat (Co-EDAF) sebagai senyawa pembawa dengan metode polymer inclusion membrane (PIM) telah dilakukan. Studi ini bertujuan untuk mengetahui pengaruh konsentrasi plasticizer, jenis dan konsentrasi garam, stabilitas membran PIM dengan pemakaian berulang dan umur membran. Membran dipreparasi dengan melarutkan Co-EDAF 8%, polivinil klorida (PVC) dan dibenzileter (DBE) ke dalam pelarut tetrahidrofuran (THF). Penentuan konsentrasi fenol sesudah proses transpor dilakukan dengan metode spektrofotometri UV-Vis menggunakan pereaksi 4-aminoantipirin dan absorbansinya diukur pada panjang gelombang 456 nm. Hasil penelitian menunjukkan bahwa fenol tertranspor secara efektif menggunakan membran Co-EDAF 8% dengan konsentrasi plasticizer 0,3132 g yaitu 84,39% dengan persentase membran yang hilang 21,29%. Penambahan garam di fasa sumber yang mampu menghasilkan fenol sebesar 81,24% adalah garam NaNO3. Transpor fenol dengan melakukan penambahan NaNO3 0,001 M di fasa sumber dan penerima menghasilkan fenol yang tertranspor sebanyak 82,41% dan 77,73%. Banyaknya fenol yang tertranspor ke fasa penerima menggunakan membran dengan pemakaian satu kali, dua kali, tiga kali, empat kali dan lima kali adalah 84,20; 72,10; 57; 33,88 dan 16,73%. Tanpa penambahan NaNO3, stabilitas membran hanya 19 hari tetapi dengan penambahan NaNO3 0,01 M stabilitasnya meningkat menjadi 60 hari. Kata kunci: Copoli Eugenol Dialil Ftalat (Co-EDAF), fenol, membran, PIM, stabilitas Studies on the stability and ability of phenol transport using Copoli Eugenol Dialil Phthalate (Co-EDAF) as a carrier compound using the polymer inclusion membrane (PIM) method have been carried out. This study aims to determine the effect of plasticizer concentration, salt type and concentration, PIM membrane stability with repeated use and membrane age. The membrane is prepared by dissolving 8% Co-EDAF, polyvinyl chloride (PVC) and dibenzyleter (DBE) into a tetrahydrofuran (THF) solvent. Determination of phenol concentrations after the transport process was carried out by UV-Vis spectrophotometry using 4- aminoantipirin reagents and their absorbance was measured at a wavelength of 456 nm. The results showed that phenol was transported effectively using a 8% Co-EDAF membrane with a plasticizer concentration of 0.3132 g is 84.39% with a percentage of the membrane missing 21.29%. The addition of salt in the source phase that is able to produce phenol of 81.24% is NaNO3 salt. Phenol transport by adding 0.001 M NaNO3 in the source and recipient phases produced 82.41% and 77.73%. transported phenols. The amount of phenol that is transported to the receiving phase using a membrane with the use of once, twice, three times, four times and five times is 84.20; 72.10; 57; 33.88 dan 16.73%. Without the addition of NaNO3, membrane stability is only 19 days but with the addition of 0.01 M NaNO3 the stability increases to 60 days. Keywords: Copoly Eugenol Dialil Phthalate (Co-EDAF), Phenol, Membrane, PIM, Stability

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi: FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit: AM.d Firlia Hidayah
Date Deposited: 16 Dec 2022 04:12
Terakhir diubah: 16 Dec 2022 04:12
URI: http://digilib.unila.ac.id/id/eprint/67719

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir