PENINGKATAN SIFAT FISIS DAN MEKANIS KAYU JABON (Anthocephalus cadamba) MELALUI PERLAKUAN PANAS AIR HEAT TREATMENT

LUSY, RAHMAWATI (2023) PENINGKATAN SIFAT FISIS DAN MEKANIS KAYU JABON (Anthocephalus cadamba) MELALUI PERLAKUAN PANAS AIR HEAT TREATMENT. PERTANIAN, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (181Kb) | Preview
	File PDF Skripsi Full Lusy Rahmawati.pdf Restricted to Hanya staf Download (1632Kb)
Preview	File PDF Skripsi tanpa pembahasan.pdf Download (1462Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini bertujuan untuk mengetahui pengaruh suhu perlakuan air heat treatment (170˚C, 190˚C, dan 210˚C) terhadap sifat fisis kayu jabon (Anthocephalus cadamba) serta pengaruh suhu perlakuan air heat treatment (170˚C, 190˚C, dan 210˚C) terhadap sifat mekanis kayu jabon. Kayu jabon diberikan perlakuan panas air heat treatment dengan suhu perlakuan 170˚C, 190˚C, dan 210˚C selama 4 jam. Hasil penelitian menunjukkan bahwa seiring dengan meningkatnya suhu perlakuan menyebabkan penurunan nilai (ΔE*) pada suhu 170˚C mengalami sedikit perubahan warna dikarenakan terdegradasinya zat ekstraktif pada kayu, sedangkan pada suhu 190˚C, dan 210˚C mengalami perubahan warna total. Kayu jabon juga mengalami penurunan berat, penyusutan volume, penurunan nilai kerapatan dan kadar air seiring dengan meningkatnya suhu perlakuan dan terdegradasinya polimer pada kayu serta terserapnya air yang berada pada dinding sel akibat perlakuan panas. Daya serap air dan stabilitas dimensi pada kayu juga terjadi peningkatan karena berkurangnya kemampuan sifat hidrofobik kayu. Terjadinya penurunan kuat tekan pada kayu juga akibat degradasi hemiselulosa akibat perlakuan panas dan suhu perlakuan yang semakin meningkat. Penurunan nilai kekerasan yang terjadi diakibatkan suhu perlakuan yang meningkat serta kehilangannya berat dalam jumlah cukup tinggi yang bisa melemahkan kayu. Perlakuan panas air heat treatment dapat mempengaruhi sifat fisis dan mekanis pada kayu jabon seiring dengan meningkatnya suhu perlakuan akibat terdegradasinya senyawa kimia pada kayu. This study aimed to determine the effect of air heat treatment temperature (170˚C, 190˚C, and 210˚C) on the physical properties of wood (Anthocephalus cadamba) and the effect of air heat treatment temperature (170˚C, 190˚C, and 210˚C) on the mechanical properties of jabon wood. Heat treatment of jabon wood was conducted at 170˚C, 190˚C, and 210˚C for 4 hours. The results showed that as the treatment temperature increased, the overall color changes (ΔE*) decreased. Jabon wood heat treated at 170˚C experienced a slight color change due to the degradation of extractive substances in the wood, while at 190˚C and 210˚C it experienced a total discoloration. Jabon wood also experienced a decrease in weight, volume shrinkage, decrease in density andmoisture content along with increasing treatment temperature and degradation of the polymer in the wood and absorption of water in the cell walls due to heat treatment. The water absorption capacity and dimensional stability of wood also decrease due to the reduced ability of the hydrophobic properties of wood. The decrease in compressive strength of wood is also due to hemicellulose degradation due to heat treatment and increasing treatment temperatures. The decrease in the hardness value that occurs is due to the increased treatment temperature and the loss of weight in a high enough amount that can weaken the wood. Air heat treatment can affect the physical and mechanical properties of Jabon wood as the treatment temperature increases due to the degradation of chemical compounds in the wood.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 630 Pertanian dan teknologi yang berkaitan
Program Studi:	Fakultas Pertanian dan Pascasarjana > Prodi Kehutanan
Pengguna Deposit:	2301200293 . Digilib
Date Deposited:	22 Feb 2023 03:33
Terakhir diubah:	22 Feb 2023 03:33
URI:	http://digilib.unila.ac.id/id/eprint/69801

Actions (login required)

Lihat Karya Akhir