PENGARUH DAYA DAN KECEPATAN LASER CO2 TERHADAP TINGKAT KEKASARAN PERMUKAAN DAN WARNA KAYU JABON (Anthocephalus cadamba)

Agus , Wisesa Gatra Perkasa (2023) PENGARUH DAYA DAN KECEPATAN LASER CO2 TERHADAP TINGKAT KEKASARAN PERMUKAAN DAN WARNA KAYU JABON (Anthocephalus cadamba). FAKULTAS PERTANIAN , UNIVERSITAS LAMPUNG. (Submitted)

Preview	File PDF ABSTRAK.pdf Download (141Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1230Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (976Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini bertujuan yaitu untuk mengetahui pengaruh daya laser CO2 terhadap perubahan warna dan kekasaran permukaan kayu yang terjadi pada kayu jabon (Anthocephalus cadamba). Papan kayu jabon diukir menggunakan laser CO2 dengan daya yang bervariasi, yakni 2,5 Watt, 5 Watt, 7,5 Watt, 10 Watt, dan 12,5 Watt dengan kecepatan pengerjaan 50 mm/s, 75 mm/s dan 100 mm/s. Perubahan warna diuji menggunakan colorimeter dan kekasaran permukaan kayu diuji menggunakan surface roughness tester. Hasil penelitian menunjukkan kecerahan (L*) dan kromatisasi kuning/biru (b*) pada kayu jabon mengalami penurunan seiring dengan meningkatnya daya laser. Nilai kromatisasi merah/hijau (a*) menunjukkan kenaikan pada daya laser 2,5 Watt dan setelah itu nilai kromatisitas pada daya laser yang lebih tinggi cenderung menurun. Nilai perubahan warna (ΔE*) pada kayu jabon setelah diukir dengan daya laser 2,5 – 12,5 Watt menunjukkan nilai > 12 yang berarti warna berubah total. Kekasaran permukaan kayu mengalami kenaikan seiring dengan meningkatnya daya laser yang digunakan. Berdasarkan hasil penelitian disimpulkan bahwa perubahan warna total (ΔE*) pada papan jabon yang terjadi menjadi lebih gelap, dan kekasaran permukaan kayu akan semakin meningkat. Kata kunci: laser CO2, warna, kekasaran, daya laser, kayu jabon (anthocephalus cadamba) This study aimed to determine the effect of CO2 laser power on the color change and surface roughness of jabon (Anthocephalus cadamba) wood. Jabon wood is engraved using a CO2 laser with a power of 2.5 Watt, 5 Watt, 7.5 Watt, 10 Watt and 12.5 Watt with processing speeds of 50 mm/s, 75 mm/s and 100 mm/. The color change was tested using a colorimeter, and the surface roughness was tested using a surface roughness tester. The results showed that the brightness (L*) and yellow/blue chromatization (b*) of Jabon wood decreased with increasing laser power. The red/green chromatization (a*) shows an increase in 2.5 Watt laser power while the chromaticity value at higher laser power tends to decrease. The color change (ΔE*) on jabon wood after engraved with the power of 2.5 – 12.5 Watt shows a value of > 12 or totally changed. The roughness of the wood surface increases with increasing laser power. The results show that the total color change (ΔE*) on the jabon board becomes darker, and the surface roughness of the wood increased. Keywords: CO2 Laser, Color, Roughness, Laser Power, Jabon Wood (Anthocephalus cadamba)

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 580 Tumbuh-tumbuhan, tanaman, botani, flora 600 Teknologi (ilmu terapan) > 630 Pertanian dan teknologi yang berkaitan
Program Studi:	Fakultas Pertanian dan Pascasarjana > Prodi Kehutanan
Pengguna Deposit:	2301913373 . Digilib
Date Deposited:	22 Feb 2023 06:52
Terakhir diubah:	22 Feb 2023 06:52
URI:	http://digilib.unila.ac.id/id/eprint/69847

Actions (login required)

Lihat Karya Akhir