MODIFIKASI PERMUKAAN KARBON AKTIF MAGNETIK DARI LIMBAH KULIT SINGKONG (Manihot utilissima.) UNTUK EKSTRAKSI SENYAWA ANTIBIOTIK TETRASIKLIN

SHELLY FEBI ADELIA , shellyfebi03@gmail.com (2022) MODIFIKASI PERMUKAAN KARBON AKTIF MAGNETIK DARI LIMBAH KULIT SINGKONG (Manihot utilissima.) UNTUK EKSTRAKSI SENYAWA ANTIBIOTIK TETRASIKLIN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG. (Submitted)

Preview	File PDF ABSTRAK.pdf Download (13Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1052Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (777Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK MODIFIKASI PERMUKAAN KARBON AKTIF MAGNETIK DARI LIMBAH KULIT SINGKONG (Manihot utilissima) UNTUK EKSTRAKSI SENYAWA ANTIBIOTIK TETRASIKLIN Oleh SHELLY FEBI ADELIA Residu antibiotik tetrasiklin di lingkungan semakin menjadi perhatian dalam beberapa tahun terakhir. Sehingga, dibutuhkan teknologi yang efektif, ekonomis, cepat, dan ramah lingkungan untuk menghilangkan residu antibiotik tetrasiklin. Studi saat ini berkaitan dengan ekstraksi antibiotik tetrasiklin menggunakan karbon aktif magnet ik yang dibuat dari limbah kulit singkong yang telah dimodifikasi dengan HNO3. Karbon aktif dioksidasi dengan HNO3 69% v/v dan dipanaskan pada suhu 65° C untuk meningkatkan karakteristik struktural dan gugus fungsi permukaan dari karbon aktif sehingga dapat meningkatkan ekstraksi antibiotik tetrasiklin. Selanjutnya, karbon aktif direaksikan dengan campuran larutan FeCl3 dan FeSO4 yang diikuti dengan penambahan larutan NaOH. Hasil FTIR menunjukkan adanya O-H hidroksil, C=O karboksil, C=C aromatik, dan C-O karbonil yang membuktikan berhasilnya penambahan gugus fungsi karena perlakuan dengan asam. Karakterisasi dengan SEMEDX dan XRD dilakukan untuk membuktikan bahwa magnetit telah berhasil melapis i karbon aktif magnetik. Dalam penelitian ini, ekstraksi teknik DSPE dikembangka n untuk adsorpsi dan desorpsi antibiotik tetrasiklin dari sampel air diikuti oleh analisis spektrofotometer UV-Vis. Kondisi optimal untuk adsorpsi antibiotik tetrasiklin dengan karbon aktif magnetik dengan massa adsorben 25 mg, 20 mL larutan antibiot ik tetrasiklin 5 ppm, dan waktu kontak 10 menit dengan hasil adsorpsi sebesar 70,33% dan desorpsi antibiotik tetrasiklin adalah 68,10%. Kata kunci: Antibiotik Tetrasiklin, Karbon Aktif Magnetik, DSPE, Kulit Singkong The presence of tetracycline antibiotics residue in environment has been of growing concern in recent years. Thus, there is a need for an effective, economical, fast, and environmental- friendly technology to remove tetracycline antibiotics. The current study deals with the extraction of tetracycline antibiotics using magnetic activated carbon prepared from cassava peel waste that has been modified with HNO3. Activated carbon was oxidized with HNO3 69% v/v and heated on temperature 65°C to improve the structural characteristics and enriched surface functional groups of the adsorbents for enhanced extraction antibiotic of tetracycline. Furthermore, the activated carbon was reacted with a mixture of FeCl3 and FeSO4 solution then followed by the addition of NaOH solution. FTIR displayed presence of O-H hydroxyl, C=O carboxyl, C=C aromatic, and C-O carbonyl proving efficacious attachment of the functional groups because of acid treatments. Characterization with SEM-EDX and XRD was done to confirm that magnetite has succeeded to coating on magnetic activated carbon. In this study, dispersive solid-phase extraction (DSPE) was developed for the adsorption and desorption of tetracycline antibiotic from water sample followed by Spectrophotometer UV-Vis analysis. Optimum conditions for tetracycline antibiotic adsorption with MAC was under conditions of 25 mg adsorbent, 20 mL of tetracycline antibiotic solution 5 ppm, and contact time of 10 minutes with the acquisition of 70.33% and desorption of tetracycline antibiotic was 68.10%. Keywords: Tetracycline antibiotics, Magnetic Activated Carbon, DSPE, Cassava peel

Jenis Karya Akhir:	Skripsi
Subyek:	000 Ilmu komputer, informasi dan pekerjaan umum 000 Ilmu komputer, informasi dan pekerjaan umum > 001 Ilmu pengetahuan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2301855829 . Digilib
Date Deposited:	10 Mar 2023 02:48
Terakhir diubah:	10 Mar 2023 02:48
URI:	http://digilib.unila.ac.id/id/eprint/69980

Actions (login required)

Lihat Karya Akhir