PENGARUH SUHU KALSINASI TERHADAP AKTIVITAS CaO/SiO2 DENGAN KOMPOSISI MASSA 1:3 SEBAGAI KATALIS TRANSESTERIFIKASI MINYAK KELAPA SAWIT

Nurkhalisah, . (2023) PENGARUH SUHU KALSINASI TERHADAP AKTIVITAS CaO/SiO2 DENGAN KOMPOSISI MASSA 1:3 SEBAGAI KATALIS TRANSESTERIFIKASI MINYAK KELAPA SAWIT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2679Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3002Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3003Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini telah dilakukan sintesis katalis CaO/SiO2 dari CaCO3 (batu kapur) dan silika sekam padi dengan komposisi massa 1:3 dengan metode sol gel, dan aplikasinya untuk transesterifikasi minyak kelapa sawit dengan metanol. CaCO3 dikalsinasi pada suhu 600℃ agar CaCO3 terdekomposisi menjadi CaO, selanjutnya katalis disintesis dengan penambahan CaO ke dalam larutan silika. Sebelum digunakan, katalis CaO/SiO2 dikalsinasi dengan variasi suhu 500, 600, 700, 800 dan 900℃ selama 6 jam. Analisis XRD menunjukkan katalis yang dikalsinasi pada suhu 500 dan 600℃ masih berada pada fasa amorf sedangkan pada suhu 700-900℃ sudah berada pada fasa kristalin dan persen kristalinitas tertinggi yakni sebesar 29,96% yang terdapat pada sampel katalis suhu kalsinasi 800℃. Analisis dengan SEM mengidentifikasikan morfologi ditandai dengan adanya granula dan partikel-partikel kecil disekeliling granula pada suhu kalsinasi 800℃. Uji aktivitas katalitik terbaik pada reaksi transesterifikasi ditunjukkan oleh katalis yang dikalsinasi pada suhu 800℃. Kondisi percobaan transesterifikasi diperoleh pada penggunaan nisbah metanol terhadap minyak 8:1, jumlah katalis 20%, dan waktu reaksi 10 jam pada suhu 70℃ dengan tingkat konversi minyak menjadi biodiesel maksimum yang dicapai adalah sebesar 74%. Hasil analisis dengan GC-MS menunjukkan bahwa biodiesel tidak seluruhnya terbentuk menjadi metil ester. Karakterisasi fisik biodiesel seperti densitas dan viskositas belum memenuhi standar SNI 7182:2015. Kata Kunci: katalis CaO/SiO2, metode sol gel, minyak kelapa sawit, transesterifikasi, biodiesel ABSTRACT In this study, the synthesis of CaO/SiO2 catalyst from CaCO3 (limestone) and rice husk silica with a mass composition of 1:3 by sol gel method was carried out, and its application for transesterification of palm oil with methanol. CaCO3 was calcined at 600℃ so that CaCO3 decomposed into CaO, then the catalyst was synthesized by adding CaO into silica solution. Before use, the catalyst CaO/SiO2 was calcined with temperature variations of 500, 600, 700, 800 and 900℃ for 6 hours. XRD analysis shows that the catalyst calcined at 500 and 600℃ is still in the amorphous phase while at 700-900℃ it is already in the crystalline phase and the highest percentage of crystallinity is 29.96% which is found in the 800℃ calcination temperature catalyst sample. SEM analysis identified the morphology characterized by the presence of granules and small particles around the granules at a calcination temperature of 800℃. The best catalytic activity test in the transesterification reaction was shown by the catalyst calcined at 800℃. The experimental conditions of transesterification were obtained by using oil to methanol ratio of 8:1, catalyst amount of 20%, and reaction time of 10 hours at 70℃ with the maximum conversion rate of oil to biodiesel achieved was 74%. GC-MS analysis showed that biodiesel was not completely formed into methyl esters. Physical characterization of biodiesel such as density and viscosity has not met the standards of SNI 7182: 2015. Keywords: CaO/SiO2 catalyst, sol gel method, palm oil, transesterification, biodiesel

Jenis Karya Akhir:	Skripsi
Subyek:	000 Ilmu komputer, informasi dan pekerjaan umum > 001 Ilmu pengetahuan 500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2301501386 . Digilib
Date Deposited:	06 Jun 2023 07:01
Terakhir diubah:	06 Jun 2023 07:01
URI:	http://digilib.unila.ac.id/id/eprint/71695

Actions (login required)

Lihat Karya Akhir