SINTESIS DAN KARAKTERISASI BIOFOAM DARI SELULOSA BONGGOL NANAS

Ananda Putra , Pratama (2023) SINTESIS DAN KARAKTERISASI BIOFOAM DARI SELULOSA BONGGOL NANAS. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (3502Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (5Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (5Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Tanaman nanas merupakan salah satu tanaman buah yang banyak dibudidayakan di Indonesia yang memiliki kandungan serat tinggi. Kandungan serat yang tinggi membuatnya sulit didekomposisi yang membuat banyak limbahnya dibuang tanpa diolah lebih lanjut. Hal ini yang menjadi pendorong untuk memanfaatkan limbah-limbah tersebut sebagai pengganti styrofoam yang disebut biodegradable foam atau biofoam. Karena besarnya dampak buruk yang ditimbulkan oleh penggunaan styrofoam, maka harus dilakukan upaya untuk mencari alternatif bahan pengemas lain yang lebih ramah lingkungan serta tidak berbahaya terhadap kesehatan manusia. Penelitian ini bertujuan untuk mengetahui pengaruh selulosa bonggol nanas pada sifat mekanis biofoam. Proses pembuatan biofoam dilakukan menggunakan teknik thermopressing dengan waktu pencetakan 5-10 menit dan suhu 200oC dengan mencampurkan variasi perbandingan tapioka : selulosa bonggol nanas (4:0, 3:1, dan 1:3), Polivinil alcohol (PVA), Mg stearate, gliserol, dan air. Karakterisasi biofoam meliputi kuat tarik, kuat tekan, dan daya serap air. Hasil penelitian menunjukkan bahwa biofoam dengan variasi perbandingan tapioka dan selulosa bonggol nanas (3:1) dengan kuat tarik pada biofoam sebesar 4,24 N/mm2, kuat tekan 5,63 N/mm2, dan daya serap air 22%. Kata kunci: Biofoam, Thermopressing, Selulosa, Bonggol Nanas, Styrofoam. Pineapple plant is a fruit plant that is widely cultivated in Indonesia which has a high fiber content. The high fiber content makes it difficult to decompose, which causes a lot of waste to be disposed of without further processing. This is the driving force for utilizing these wastes as a substitute for styrofoam which is called biodegradable foam or biofoam. Due to the large adverse effects caused by the use of styrofoam, efforts must be made to find alternative packaging materials that are more environmentally friendly and not harmful to human health. This study aims to determine the effect of pineapple hump cellulose on the mechanical properties of biofoam. The process of making biofoam was carried out using a thermopressing technique with a printing time of 5-10 minutes and a temperature of 200oC by mixing various ratios of tapioca: pineapple hump cellulose (4:0, 3:1, and 1:3), Polivinil alcohol (PVA), Mg stearate, glycerol, and water. Characterization of biofoam includes tensile strength, compressive strength, and water absorption. The results showed that biofoam with variations in the ratio of tapioca and pineapple hump cellulose (3:1) with a tensile strength of 4.24 N/mm2 on biofoam, a compressive strength of 5.63 N/mm2, and a water absorption capacity of 22%. Keywords: Biofoam, Thermopressing, Cellulose, Pineapple Hump, Styrofoam.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2301797046 . Digilib
Date Deposited:	22 Jun 2023 01:42
Terakhir diubah:	22 Jun 2023 01:42
URI:	http://digilib.unila.ac.id/id/eprint/72857

Actions (login required)

Lihat Karya Akhir