PERLAKUAN PANAS PRESIPITASI HARDENING DENGAN VARIASI LAMA WAKTU NATURAL AGING PADA MATERIAL PADUAN ALUMUNIUM SERI 6061

Dasuri, - (2023) PERLAKUAN PANAS PRESIPITASI HARDENING DENGAN VARIASI LAMA WAKTU NATURAL AGING PADA MATERIAL PADUAN ALUMUNIUM SERI 6061. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRACT DASURI_1615021016.pdf Download (299Kb) | Preview
	File PDF SKRIPSI FULL DASURI_1615021016.pdf Restricted to Hanya staf Download (4Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN DASURI_1615021016.pdf Download (3605Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Tujuan dari penelitian ini adalah untuk mengetahui pengaruh waktu natural aging terhadap nilai kekerasan dan perubahan mikrostruktur paduan aluminium seri 6061. Material yang digunakan dalam penelitian ini adalah Al-6061 dengan dimensi 40×30×10 cm, kemudian panas. diberi perlakuan suhu 550℃ selama 1 jam, kemudian diquenching dengan air kemudian diberi perlakuan natural aging dengan variasi 2 hari, 7 hari dan 14 hari. Hasil komposisi kimia yang diperoleh dengan menggunakan Spectromax menunjukkan persentase Si dalam 1,07 n Mg adalah 1,5%. Hasil uji kekerasan Rockwell tanpa perlakuan panas adalah 60,52 (HRE) dan setelah quenching 37,30 (HRE). Nilai kekerasan tertinggi terdapat pada variasi 7 hari dengan nilai kekerasan 72,02 (HRE). Jika nilai kekerasan dengan variasi waktu 7 hari meningkat sebesar 9% dari kekerasan material tanpa perlakuan panas. Pada kondisi ini diperoleh hasil kekerasan yang optimal dibandingkan dengan hasil struktur mikro setelah 2 hari dan 14 hari. Kata kunci: Aluminium 6061, Penuaan alami, kekerasan dan struktur mikro. The purpose of this study is to investigate the effect of natural aging time on the hardness value and microstructural changes of aluminum alloy 6061 series. The material used in this study was Al-6061 with dimensions of 40 × 30 × 10 cm, then heat treatment at 550 °C for 1 hour, then water quenching, and then natural aging treatment with time variation. 2 days, 7 days and 14 days. Chemical composition results obtained using Spectromax showed a Si percentage of 1.07% and a Mg content of 1.5%. The Rockwell hardness test results show a hardness value of 60.52 (HRE) without heat treatment and 37.30 (HRE) after quenching. The highest hardness value is found in the 7-day variation with a hardness value of 72.02 (HRE). If the hardness value with a time variation of 7 days increased by 9% of the material hardness without heat treatment. In this mode, optimal hardness results are obtained compared to microstructure results with 2- and 14-day time variations. Keywords: Aluminum 6061, Natural aging, hardness and microstructure.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	2301878128 . Digilib
Date Deposited:	04 Jul 2023 07:04
Terakhir diubah:	04 Jul 2023 07:04
URI:	http://digilib.unila.ac.id/id/eprint/73327

Actions (login required)

Lihat Karya Akhir