PENGARUH VARIASI KONSENTRASI Zn(NO3)2 6H2O TERHADAP GUGUS FUNGSI, UKURAN PARTIKEL, DAN MORFOLOGI PARTIKEL NANOPARTIKEL ZnO DENGAN METODE SINTESIS HIJAU MENGGUNAKAN EKSTRAK DAUN KELOR

CHAIRUNISSA ANANDA , BENYAMIN (2023) PENGARUH VARIASI KONSENTRASI Zn(NO3)2 6H2O TERHADAP GUGUS FUNGSI, UKURAN PARTIKEL, DAN MORFOLOGI PARTIKEL NANOPARTIKEL ZnO DENGAN METODE SINTESIS HIJAU MENGGUNAKAN EKSTRAK DAUN KELOR. FAKULTASMATEMATIKA DAN ILMUPENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1963Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2480Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2481Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mengetahui pengaruh variasi konsentrasi Zn(NO3)2•6H2O (seng nitrat heksahidrat) terhadap gugus fungsi, ukuran partikel, dan morfologi partikel nanopartikel ZnO dengan metode sintesis hijau menggunakan daun kelor. Bahan-bahan yang digunakan dalam penelitian ini yaitu ekstrak daun kelor sebagai bahan utama dalam metode sintesis hijau, Zn(NO3)2•6H2O dengan variasi konsentrasi 0,2; 0,4; 0,6; dan 0,8 M sebagai prekursor, NaOH dan etanol sebagai pelarut prekursor. Berdasarkan hasil karakterisasi menggunakan FTIR menunjukkan bahwa gugus fungsi dalam kandungan daun kelor berperan dalam pembentukan nanopartikel ZnO. Sedangkan hasil karakterisasi XRD menunjukkan perbedaan difraktogram dengan standar ZnO pada konsentrasi Zn(NO3)2•6H2O 0,6 M dan 0,8 M dengan munculnya fasa NNaO3. Hasil karakterisasi SEM menunjukkan bahwa morfologi nanopartikel ZnO dengan metode sintesis hijau berbentuk acak. Kata kunci: Daun kelor, Zn(NO3)2•6H2O, nanopartikel ZnO, sintesis hijau. This research was conducted to determine the effect of varying concentrations of Zn(NO3)2•6H2O (zinc nitrate hexahydrate) on functional groups, particle size, and particle morphology of ZnO nanoparticles using the green synthesis method using Moringa leaves. The materials used in this study were moringa leaf extract as the main ingredient in the green synthesis method, Zn(NO3)2•6H2O with various concentrations of 0.2; 0.4; 0.6; and 0.8 M as precursor, NaOH and ethanol as precursor solvents. Based on the results of characterization using FTIR, it shows that the functional groups in the content of Moringa leaves play a role in the formation of ZnO nanoparticles. Meanwhile, the results of the XRD characterization showed a diffractogram difference with standard ZnO at concentrations of 0.6 M and 0.8 M Zn(NO3)2•6H2O with the appearance of the NNaO3 phase. SEM characterization results show that the morphology of ZnO nanoparticles using the green synthesis method is irregular in shape. Keywords: Moringa leaves, Zn(NO3)2•6H2O, ZnO nanoparticles, green synthesis

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2301412482 . Digilib
Date Deposited:	31 Jul 2023 01:37
Terakhir diubah:	31 Jul 2023 01:37
URI:	http://digilib.unila.ac.id/id/eprint/73836

Actions (login required)

Lihat Karya Akhir