KONVERSI MINYAK KELAPA SAWIT (Elaeis giuneensis J.) MENJADI SENYAWA NITROGEN DAN UJI AKTIVITASNYA SEBAGAI GREEN INHIBITOR KOROSI BAJA LUNAK

Laila , Hidayah (2023) KONVERSI MINYAK KELAPA SAWIT (Elaeis giuneensis J.) MENJADI SENYAWA NITROGEN DAN UJI AKTIVITASNYA SEBAGAI GREEN INHIBITOR KOROSI BAJA LUNAK. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2609Kb) | Preview
	File PDF TESIS FULL.pdf Restricted to Hanya staf Download (2908Kb) | Minta salinan
Preview	File PDF TESIS TANPA BAB PEMBAHASAN.pdf Download (2909Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mempelajari sintesis senyawa nitrogen dari minyak sawit dan penerapan produk tersebut sebagai inhibitor korosi pada baja ringan dalam larutan air garam jenuh CO2. Sintesis senyawa nitrogen dilakukan dalam dua tahap. Tahap pertama adalah konversi minyak sawit menjadi metil ester melalui transesterifikasi minyak sawit dengan metanol menggunakan zeolit-A dari hasil sintesa silika sekam padi dan aluminium foil sebagai katalis. Metil ester yang diperoleh kemudian direaksikan dengan dietanolamina menggunakan zeolit-A dan natrium metoksida (NaOCH3) yang baru dibuat dari NaOH (Pa) dan metanol (Pa) sebagai katalis. Kedua katalis tersebut dikarakterisasi menggunakan beberapa teknik, dimana zeolit-A dikarakterisasi menggunakan XRD dan SEM, sedangkan NaOCH3 dikarakterisasi menggunakan FTIR, XRD, dan SEM. Senyawa metil ester dan senyawa nitrogen dianalisis menggunakan FTIR dan GC-MS. Aktivitas senyawa nitrogen sebagai inhibitor korosi dievaluasi menggunakan metode Wheel test dan SEM untuk memvisualisasikan permukaan sampel logam yang diberi senyawa nitrogen yang dihasilkan, dibandingkan dengan sampel asli dan sampel yang diberi perlakuan tanpa inhibitor. Hasil percobaan menunjukkan bahwa asam lemak dalam minyak sawit berhasil diubah seluruhnya menjadi metil ester yang sesuai. Analisis GC-MS menunjukkan terbentuknya senyawa nitrogen dengan persentase relatif tertinggi sebesar 63,7% dihasilkan dari reaksi menggunakan katalis NaOCH3. Percobaan korosi menunjukkan bahwa penggunaan senyawa nitrogen 150 ppm sebagai inhibitor mampu memberikan efisiensi penghambatan sebesar 96,85%. Aktivitas yang menjanjikan ini sesuai dengan hasil SEM yang menunjukkan permukaan sampel terlindungi dengan baik. Kata kunci: Senyawa nitrogen, minyak kelapa sawit, inhibitor korosi, baja lunak, larutan garam. This research was conducted to study synthesis of nitrogen compounds from palm oil and application of the product as corrosion inhibitor for mild steel in CO2 saturated brine solution. The synthesis of nitrogen compounds was conducted in two stages. The first stage was conversion of palm oil into methyl esters by transesterification of the oil with methanol using zeolite-A synthesized from rice husk silica and aluminum foil as catalyst. The methyl esters obtained were then reacted with diethanolamine using zeolite-A and sodium methoxide (NaOCH3) frehsly prepared from reagent grade NaOH and methanol as catalysts. Both catalysts were characterized using several techniques, in which zeolite-A was characterized using XRD and SEM, whiled NaOCH3 was characterized using FTIR, XRD, and SEM. The methyl esters and nitrogen compounds were analysed using FTIR and GC-MS. The activity of the nitrogen compounds as corrosion inhibitor was evaluated using wheel test method and SEM to visualize the surface of the metal sample treated with nitrogen compounds produced, compared to those of the original and treated sample without inhibitor. The experimental results revealed that fatty acids in palm oil were completely converted into their corresponding methyl esters. The GC-MS analysis confirmed the formation of nitrogen compounds with the highest relative percentage of 63.7% was produced from the reaction using NaOCH3 as catalyst. The corrosion inhibition experiments revealed that the use of 150 ppm of nitrogen compounds as inhibitor was able to provide inhibition efficiency as high as 96.85%. This promising activity is in agreement with the SEM result which indicated the the surface of sample was well protected. Key words: Nitrogen compunds, palm oil, corroson inhibitor, mild steel, brine solution.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Magister Ilmu Kimia
Pengguna Deposit:	2308515628 . Digilib
Date Deposited:	16 Oct 2023 02:23
Terakhir diubah:	16 Oct 2023 02:23
URI:	http://digilib.unila.ac.id/id/eprint/76447

Actions (login required)

Lihat Karya Akhir