PENGARUH VARIASI TEMPERATUR DAN WAKTU TAHAN TERHADAP REDUKSI KARBOTERMIK BIJIH MANGAN MENGGUNAKAN REDUKTOR GRAFIT

HILYA SOFWATUZ , ZAHRA (2024) PENGARUH VARIASI TEMPERATUR DAN WAKTU TAHAN TERHADAP REDUKSI KARBOTERMIK BIJIH MANGAN MENGGUNAKAN REDUKTOR GRAFIT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (9Mb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (9Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (9Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Mangan merupakan salah satu mineral yang banyak ditemukan di Indonesia. Salah satu metode pengolahan bijih mangan adalah pirometalurgi dengan proses reduksi karbotermik. Proses reduksi ini memerlukan temperatur dan waktu tahan yang tepat agar energi yang digunakan selama proses reduksi bijih mangan dapat berlangsung secara optimal. Untuk itu perlu dilakukan penelitian lebih lanjut tentang bagaimana pengaruh dari kedua hal tersebut. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh variasi temperatur dan waktu tahan reduksi karbotermik bijih mangan terhadap recovery (pemulihan), perubahan fasa yang terjadi serta morfologi dan komposisi unsur pada bijih mangan. Pada penelitian ini, metode yang digunakan adalah pirometalurgi dengan variasi temperatur dan waktu tahan 950 ºC, 1050 ºC, 1150 ºC dan 30, 60, 90 menit dengan menggunakan reduktor grafit dan aditif Na2SO4. Sampel dikarakterisasi dengan menggunakan X-Ray Fluorosence (XRF), X-Ray Diffraction (XRD) dan Scanning Electron Microscopy–Energy Dispersive Spectroscopy (SEM-EDS). Hasil analisa menunjukkan bahwa pemulihan mangan tertinggi terjadi pada temperatur 950 ºC dengan waktu tahan 90 menit dengan kadar mangan sebesar 84,432 %. Perubahan fasa yang terjadi menunjukkan bahwa bijih mangan tereduksi secara bertahap pada setiap peningkatan temperatur dan waktu tahan. Dimana perubahan fasa ini didasarkan pada kinetika reduksi oksida mangan (MnO2 → Mn3O4 → MnO) dan oksida besi (Fe2O3 → Fe3O4 → Fe). Adanya variasi temperatur dan waktu tahan juga mempengaruhi morfologi dan komposisi unsur pada bijih mangan. Kata Kunci: bijih mangan, reduksi karbotermik, temperatur, waktu tahan ABSTRACT Manganese is one of the minerals found in Indonesia. One method of processing manganese ore is called pyrometallurgy with carbothermic reduction process. This reduction process requires the right temperature and the right holding time so that the energy used during the reduction process of manganese ore can be done optimally. It is necessary to conduct further research on how temperature and holding time affect the processing of manganese ore. The purpose of this study is to determine the effect of temperature variation and resistance time of manganese ore carbothermic reduction on recovery, phase changes that occur as well as morphology and elemental composition in manganese ore. The methodology used in this researsh was called pyrometallurgy with some variations in temperature (950 ºC, 1050 ºC, 1150 ºC) and the holding time (30, 60, 90 minutes) using graphite reductant and Na2SO4 additive. The samples were characterized using X-Ray Fluorosence (XRF), X-Ray Diffraction (XRD) and Scanning Electron Microscopy –Energy Dispersive Spectroscopy (SEM-EDS). The analysis showed that the highest manganese recovery occurred at a temperature of 950 ºC with a holding time of 90 minutes with a manganese content of 84.432 %. The phase changes that occur indicate that manganese ore is gradually reduced at each increase in temperature and holding time. This phase change is based on the reduction kinetics of manganese oxide (MnO2 → Mn3O4 → MnO) and iron oxide (Fe2O3 → Fe3O4 → Fe). Variations of temperature and holding time also affect the morphology and elemental composition of manganese ore. Keywords: manganese ore, carbothermic reduction, temperature, holding time

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2308964805 . Digilib
Date Deposited:	01 Feb 2024 08:28
Terakhir diubah:	01 Feb 2024 08:28
URI:	http://digilib.unila.ac.id/id/eprint/78475