PENGARUH VARIASI KOMPOSISI BASALT TERHADAP PEMBENTUKAN CELLULAR GLASS CERAMIC MELALUI METODE DIRECT FOAMING

NUR , ANNISA (2023) PENGARUH VARIASI KOMPOSISI BASALT TERHADAP PEMBENTUKAN CELLULAR GLASS CERAMIC MELALUI METODE DIRECT FOAMING. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (2661Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3042Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3041Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Dalam era konstruksi modern, kebutuhan akan gedung tinggi sebagai solusi efisien lahan perkotaan semakin mendesak. Oleh karena itu diperlukan solusi inovatif dengan menggunakan material ringan, seperti cellular glass ceramic, untuk mengatasi beban struktural tinggi, meningkatkan efisiensi energi, dan menyederhanakan proses konstruksi pada gedung tinggi. Penelitian ini menggunakan metode direct foaming dengan variasi bahan polyurethane (PU) sebesar 30%, 40%, dan 50% sebagai bahan pembusa. Batu basalt berasal dari Mataram Baru, Lampung Timur. Sedangkan fly ash berasal dari PLN Tarahan, Lampung Selatan. Sampel dilakukan variasi komposisi 50:50%, 60:40%, 70:30%, 80:20%, dan 90:10%. Proses dilakukan dengan pemanasan pada suhu 400°C, 700°C, dan 950°C selama 2 jam, dengan pendinginan di dalam tungku. Hasil karakterisasi dan uji mekanis serta fisis menunjukkan bahwa cellular glass ceramic yang dibuat dengan bahan basalt dan fly ash dengan polyurethane foam sebagai foaming agent memberikan hasil yang didominasi oleh SiO_2, AI_2 O_3, Fe_2 O_3 dan CaO dengan fase kristal tertinggi yaitu anorthite, albite, dan nepheline. Dalam konteks kuat tekan, sampel yang didominasi oleh basalt menunjukkan kuat tekan yang semakin besar. Hasil karakterisasi SEM pada sampel 50B7F3 menunjukkan jumlah pori tertinggi dengan ukuran ≤ 1mm sekitar 80% dan ≥ 1 mm sekitar 20%. Keywords: cellular glass ceramic, basalt, fly ash , foaming agent, polyurethane. In the modern construction era, the need for tall buildings as an efficient solution for urban land is increasingly urgent. Therefore, innovative solutions are needed using lightweight materials, such as cellular glass ceramic, to overcome high structural loads, increase energy efficiency, and simplify the construction process in tall buildings.. This research uses the direct foaming method with variations in polyurethane (PU) material of 30%, 40% and 50% as the foaming agent. Basalt stone comes from Mataram Baru, East Lampung. Meanwhile, fly ash comes from PLN Tarahan, South Lampung. Samples had composition variations of 50:50%, 60:40%, 70:30%, 80:20%, and 90:10%. The process is carried out by heating at temperatures of 400°C, 700°C, and 950°C for 2 hours, with cooling in the furnace. The results of characterization and mechanical and physical tests show that cellular glass ceramic made from basalt and fly ash with polyurethane foam as a foaming agent gives results that are dominated by SiO_2, AI_2 O_3, Fe_2 O_3 and CaO with the highest crystal phases, namely anorthite, albite and nepheline. In the context of compressive strength, samples dominated by basalt show greater compressive strength. The SEM characterization results on sample 50B7F3 show the highest number of pores with a size of ≤ 1mm around 80% and ≥ 1 mm around 20%. Keywords: cellular glass ceramic, basalt, fly ash , foaming agent, poliuretan.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2308041085 . Digilib
Date Deposited:	02 Feb 2024 06:25
Terakhir diubah:	02 Feb 2024 06:25
URI:	http://digilib.unila.ac.id/id/eprint/78497

Actions (login required)

Lihat Karya Akhir