PENGARUH NANOTITANIA/NANOSENGOKSIDA (TiO /ZnO) PADA BAHAN POLIETILENA UNTUK MEMBLOK SINAR ULTRAVIOLET

Setiawan , Wawan (2024) PENGARUH NANOTITANIA/NANOSENGOKSIDA (TiO /ZnO) PADA BAHAN POLIETILENA UNTUK MEMBLOK SINAR ULTRAVIOLET. Masters thesis, UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK.pdf Download (238Kb) | Preview
	File PDF TESIS FULL.pdf Restricted to Hanya staf Download (2620Kb) | Minta salinan
Preview	File PDF TESIS FULL TANPA BAB PEMBAHASAN.pdf Download (2067Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Komposit lapisan tipis PE/TiO /ZnO telah dibuat dengan metode coating yang bertujuan untuk melihat pengaruh penambahan nano partikel TiO /ZnO pada bahan polietilena dalam memblok sinar UV yang divariasikan dengan konsentrasi masing masing nano TiO /ZnO 0; 0,1; 0,2; 0,3; 0,4 dan 0,5 g dengan masing masing ketebalan lapisan yang diinginkan yaitu 6 µm, 12 µm dan 25 µm. Karakterisasi nano TiO dan nano ZnO menggunakan analisis X-Ray Diffraction diperoleh data bahwa ukuran nano TiO 5,77 nm dan nano ZnO 16 nm dengan struktur kristal yang terbentuk adalah anatase dan wurzite. Struktur komposit yang dihasilkan memiliki semua material yang diharapkan, dan terjadi interaksi antara PE, TiO , dan ZnO dalam lapisan tipis yang dihasilkan berdasarkan uji Fourier Transform Infrared. Penambahan konsentrasi nano TiO dan nano ZnO mampu efektif dalam meningkatkan ketahanan terhadap sinar ultraviolet pada bahan polietilena berdasarkan uji menggunakan ultraviolet light meter. Pengaruh penambahan nano TiO dan nano ZnO pada bahan polietilena untuk memblok sinar ultraviolet yaitu semakin besar penambahan konsentrasi nanopartikel TiO dan ZnO maka berpengauh dalam memblok sinar UV. Lapisan tipis PE/ TiO /ZnO memiliki struktur morfologi yang mendukung fungsi sebagai lapisan pelindung UV. Meskipun terdapat aglomerasi partikel, distribusi partikel secara keseluruhan cukup merata dalam matriks PE, memungkinkan lapisan untuk memberikan perlindungan yang optimal terhadap sinar UV. Penambahan nano TiO₂ dan ZnO dalam lapisan tipis PE secara signifikan meningkatkan koefisien serapan UV pada berbagai ketebalan lapisan sedangkan ketebalan lapisan tipis juga berpengaruh secara signifikan pada tahanan dalam memblok sinar UV Kata kunci: nano TiO , nano ZnO, polietilena, sinar UV. A PE/TiO /ZnO thin film composite has been created using the coating method. This research aims to observe the effect of adding TiO /ZnO nanoparticles to polyethylene materials in blocking UV rays, with variations in the concentration of each TiO /ZnO nanoparticle at 0; 0,1; 0,2; 0,3; 0,4 and 0,5 g, with each desired layer thickness being 6 µm, 12 µm, and 25 µm. The characterization of TiO and ZnO nanoparticles using XRay Diffraction analysis revealed that the size of TiO nanoparticles is 4.3 nm and ZnO nanoparticles is 16 nm, with the crystal structures formed being anatase and wurtzite. The resulting composite structure contains all the expected materials, and interactions between PE, TiO , and ZnO are observed in the thin layer based on Fourier Transform Infrared testing. The addition of TiO and ZnO nanoparticles effectively increases the resistance to ultraviolet rays in polyethylene materials based on testing using an ultraviolet light meter. The effect of adding TiO and ZnO nanoparticles to polyethylene materials to block ultraviolet rays is that the higher the concentration of TiO and ZnO nanoparticles, the more effective the UV blocking. The PE/ TiO /ZnO thin layer has a morphological structure that supports its function as a UV protective layer. Although there is particle agglomeration, the overall particle distribution is fairly even in the PE matrix, allowing the layer to provide optimal protection against UV rays. The addition of TiO₂ and ZnO nanoparticles in the PE thin layer significantly increases the UV absorption coefficient at various layer thicknesses, while the thin layer thickness does not significantly affect resistance in blocking UV rays Keyword: nano TiO , nano ZnO, polyethylene UV rays.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	600 Teknologi (ilmu terapan) > 602 Aneka ragam tentang teknologi dan ilmu terapan 600 Teknologi (ilmu terapan) > 607 Pendidikan, riset, topik terkait 600 Teknologi (ilmu terapan) > 660 Teknik kimia
Program Studi:	FAKULTAS MIPA > Prodi Magister Ilmu Fisika
Pengguna Deposit:	2308388712 . Digilib
Date Deposited:	19 Dec 2024 08:33
Terakhir diubah:	19 Dec 2024 08:33
URI:	http://digilib.unila.ac.id/id/eprint/80894

Actions (login required)

Lihat Karya Akhir