PENGUJIAN SIFAT MEKANIK DAN BIODEGRADASI GLASS-CERAMICS

Syaipudin , Anwar (2024) PENGUJIAN SIFAT MEKANIK DAN BIODEGRADASI GLASS-CERAMICS. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - syaipudin anwar.pdf Download (87Kb) | Preview
	File PDF Thesis FULL - syaipudin anwar.pdf Restricted to Hanya staf Download (3288Kb) | Minta salinan
Preview	File PDF Thesis tanpa bab pembahasan- syaipudin anwar.pdf Download (2219Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Glass-ceramics merupakan material polikristalin berbutir halus yang dihasilkan oleh kristalisasi terkontrol pada fasa glass. Memiliki karaktesitik sebagai material biokeramik yang tahan terhadap bahan kimia maupun cairan tubuh, tahan korosi, dan sifat mekanik unggul. Material yang dikembangkan menjadi glass-ceramics adalah basalt. Pembuatan glass-ceramics diawali dengan pembentukan glass melalui proses melting temperatur 1.200 oC selama 2 jam dilanjutkan pendinginan secara cepat. Material glass selanjutnya dihancurkan dan diayak menggunakan mesh 325. Material glass yang sudah dihaluskan dicampurkan dengan asam borat. Selanjutnya pembentukan nukleasi dengan perlakuan panas temperatur 600 oC selama 2 jam, dan proses kristalisasi pada temperature 950 oC selama 3 jam. Hasil analisis thermal menunjukkan bahwa basal dengan penambahan asam borat 20% berpengaruh terhadap menurunnya suhu kristalisasi. Batuan basalt memiliki temperatur kristalisasi sebesar 1.100°C. Batuan basal yang ditambahkan asam borat 20% memiliki temperature kristalisasi sebesar 950°C. Komposisi kimia glass- ceramics dominan 37,702 wt% - 43,539wt% SiO2; 10,133 wt% - 13.223 wt% Al2O3 ; 19,793 wt% - 25,48 wt% Fe2O3; 12,079 wt% - 21,228 CaO, dan 3,036 wt% - 6,569 wt% MgO. Fasa yang terbentuk yaitu pyroxene, anorthite, dan pigeonite. Kuat tekan sebesar 1.001,51 N hingga 12.721,3 N dengan densitas antara 0,42 hingga 1,69 g/cm3 . Porositas yang terbentuk yaitu 9 hingga 24,66 %. Pengujian degradasi dengan perendaman NaCl 0,9% menghasilkan perubahan berat sebesar 0,50% hingga 0,99 %. Pengujian degradasi dengan NaCl 0,9% yang ditambahkan laju aliran 1,86 liter per menit menghasilkan perubahan berat sebesar 0,11% hingga 2,75 %. Kata Kunci: basalt, glass, asam borat, glass-ceramics, kuat tekan, degradasi Glass-ceramics is a fine-grained polycrystalline material produced by controlled crystallization of the glass phase. It has the characteristics of a bioceramic material that is resistant to chemicals and body fluids, corrosion resistant, and superior mechanical properties. The material developed into glass-ceramics is basalt. The manufacture of glass-ceramics begins with the formation of glass through a melting process at a temperature of 1,200 oC for 2 hours followed by rapid cooling. The glass material is then crushed and sieved using 325 mesh. The pulverized glass material is mixed with boric acid. Furthermore, the formation of nucleation with heat treatment at a temperature of 600 oC for 2 hours, and crystallization process at a temperature of 950 oC for 3 hours. The results of thermal analysis show that basalt with the addition of 20% boric acid has an effect on decreasing the crystallization temperature. Basalt rock has a crystallization temperature of 1100 °C. Basalt rock to which 20% boric acid is added has a crystallization temperature of 950°C. The chemical composition of glass-ceramics is dominant 37.702 wt% - 43.539 wt% SiO2; 10.133 wt% - 13.223 wt% Al2O3; 19.793 wt% - 25.48 wt% Fe2O3; 12.079 wt% - 21.228 CaO, and 3.036 wt% - 6.569 wt% MgO. The phases formed are pyroxene, anorthite, and pigeonite. The compressive strength is 1.001,51 N to 12.721,3 N with a density between 0.42 to 1.69 g/cm3. The porosity formed is 9 to 24.66%. Degradation testing with 0.9% NaCl immersion resulted in weight changes of 0.50% to 0.99%. Degradation testing with 0.9% NaCl added at a flow rate of 1.86 liters per minute resulted in weight changes of 0.11% to 2.75%. Keywords; basalt,glass, borid acid, glass-cermics, compressive test, degradation

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi Magister Teknik Mesin
Pengguna Deposit:	UPT . Siswanti
Date Deposited:	07 Mar 2025 07:51
Terakhir diubah:	07 Mar 2025 07:51
URI:	http://digilib.unila.ac.id/id/eprint/85692

Actions (login required)

Lihat Karya Akhir