PENGARUH ARUS LAS TERHADAP KEKUATAN IMPAK DAN STRUKTUR MIKRO HASIL PENGELASAN SMAW PADA BAJA AISI 1020

ALDO PUTRA, SINGURA (2024) PENGARUH ARUS LAS TERHADAP KEKUATAN IMPAK DAN STRUKTUR MIKRO HASIL PENGELASAN SMAW PADA BAJA AISI 1020. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK SKRIPSI_ALDO PUTRA SINGURA - Aldo Putra Singura.pdf Download (34Kb) | Preview
	File PDF SKRIPSI FULL_ALDO PUTRA SINGURA Tanpa Lampiran - Aldo Putra Singura.pdf Restricted to Hanya staf Download (2785Kb) | Minta salinan
Preview	File PDF SKRIPSI_ALDO PUTRA SINGURA Tanpa Pembahasan dan Lampiran - Aldo Putra Singura.pdf Download (1865Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Baja AISI 1020 adalah salah satu material baja karbon rendah yang sedang banyak digunakan sebagai bahan utama pada pembuatan elemen mesin seperti poros, roda gigi, baut, pipa, kopling, dan rangka mesin. Penelitian ini bertujuan untuk mengetahui pengaruh variasi kuat arus pada proses pengelasan terhadap sifat mekanik dan struktur mikro baja AISI 1020. Penelitian ini menggunakan spesimen berupa baja AISI 1020 yang diberikan perlakuan pengelasan SMAW dengan variasi kuat arus 90A, 120A dan 150A, kemudian didinginkan selama 24 jam, lalu dipotong dan dibentuk spesimen uji impak mengikuti standar ASTM E- 23. Selanjutnya dilakukan pengujian impak metode charpy dan pengamatan struktur mikro dari hasil uji impak yang tertinggi dan terendah. Hasil pengujian impak didapatkan energi impak sebelum dilakukan perlakuan pengelasan adalah sebesar 96 Joule. Hasil energi impak setelah dilakukan perlakuan pengelasan SMAW dengan variasi kuat arus las 90A, 120A dan 150A sebesar 75,33 Joule, 67,67 Joule, 58 Joule. Pada pengamatan struktur mikro menggunakan Optical Microscopy (OM) menunjukkan perubahan bentuk pada ukuran butir dan distribusi fasa pada struktur mikro dari tanpa perlakuan dan yang telah mengalami perlakuan pengelasan SMAW dengan kuat arus yang berbeda. Dapat disimpulkan bahwa semakin tinggi kuat arus yang diberikan dalam proses pengelasan pada baja AISI 1020, maka kekuatan impaknya akan semakin menurun sebesar 39,6% dari raw material. Hal ini disebabkan oleh perubahan struktur mikro dan sifat mekanik baja akibat pengaruh panas yang lebih besar pada arus lebih tinggi. Kata kunci : Baja AISI 1020, Variasi kuat arus las, Pengelasan SMAW, ketangguhan uji impak dan OM. AISI 1020 steel is one of the low carbon steel materials that is being widely used as the main material in the manufacture of machine elements such as shafts, gears, bolts, pipes, couplings, and engine frames. This study aims to determine the effect of variations in current strength in the welding process on the mechanical properties and microstructure of AISI 1020 steel. This study uses specimens in the form of AISI 1020 steel which is given SMAW welding treatment with variations in current strength of 90A, 120A and 150A, then cooled for 24 hours, then cut and formed impact test specimens following ASTM E-23 standards. Furthermore, the charpy method of impact testing and observation of the microstructure of the highest and lowest impact test results were carried out. The impact test results obtained impact energy before welding treatment is 96 Joules. The results of impact energy after SMAW welding treatment with variations in welding current strength of 90A, 120A and 150A amounted to 75.33 Joules, 67.67 Joules, 58 Joules. In the observation of microstructure using Optical Microscopy (OM) shows changes in grain size and phase distribution in the microstructure from without treatment and those that have undergone SMAW welding treatment with different current strengths. It can be concluded that the higher the current strength given in the welding process on AISI 1020 steel, the impact strength will decrease by 39.6% from the raw material. This is due to changes in the microstructure and mechanical properties of the steel due to the influence of greater heat at higher currents. Keywords: AISI 1020 steel, Welding current variation, SMAW welding, impact toughness test and OM.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) 600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Dito Nipati
Date Deposited:	15 Apr 2025 09:36
Terakhir diubah:	15 Apr 2025 09:36
URI:	http://digilib.unila.ac.id/id/eprint/86089

Actions (login required)

Lihat Karya Akhir