SINTESIS NANO ZnO MENGGUNAKAN EKSTRAKDAUNJAMBU BIJI (Phidium guajava L)

Putri, Vidia Citra (2024) SINTESIS NANO ZnO MENGGUNAKAN EKSTRAKDAUNJAMBU BIJI (Phidium guajava L). Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF 5. ABSTRAK TESIS PUTRI VIDIA CITRA - Putri Vidia Citra.pdf Download (177Kb) | Preview
	File PDF Revisi - FULL, BAB 3, KESIMPULAN, DAFTAR PUSTAKA - Putri Vidia Citra.pdf Restricted to Hanya staf Download (3190Kb) | Minta salinan
Preview	File PDF TESIS - PUTRIVIDIA CITRA (2027041006) - Putri Vidia Citra.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan pembuatan nano ZnO menggunakan ekstrak daun jambubiji. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan ekstrakdaunjambu biji terhadap struktur dan morfologi nano ZnO dan mengetahui ukurannano ZnO yang terbentuk. Variasi ekstrak daun jambu biji yang digunakanyaitu10 ml, 20 ml, 30 ml, 40 ml dan 50 ml. Karakterisasi yang digunakanialahDifraksi Sinar-X (XRD), Scanning Electron Microscopy (SEM) dan dilakukanjuga uji antibakteri. Hasil karakterisasi XRD menunjukkan fasa yang terbentukialah fasa Wurtzite, dengan ukuran partikel paling besar pada sample ZnO-10yaitu 27,78 nm. Hasil karakterisasi SEM menunjukkan struktur yang terbentukpada penelitian ini yaitu heksagonal dengan morfologi nano ZnOyang berbentukbola kristal. Nano ZnO teruji dapat menjadi antibakteri dengan dilakukannyapengujian dengan metode difusi dan didapatkan zona hambat paling besar padasample ZnO-20 sebesar 8,3 mm. Kata kunci: ZnO, ekstrak daun jambu biji, XRD, SEM, antibakteri Nano ZnO has been made using guajava leaf extract. This research aims todetermine the effect of adding guajava leaf extract on the structure andmorphology of nano ZnO and determine the size of the nano ZnOformed. Variations in guajava leaf extract used were 10 ml, 20 ml, 30 ml, 40 ml and 50ml. The characterization used is X-Ray Diffraction (XRD), Scanning ElectronMicroscopy (SEM) and an antibacterial test is also carried out. The results of XRD characterization show that the phase formed is the Wurtzite phase, withthelargest particle size in the ZnO-10 sample, namely 27.78 nm. The SEMcharacterization results show that the structure formed in this study is hexagonal with a crystal ball-shaped ZnO nano morphology. Nano ZnO was tested tobeantibacterial by testing using the diffusion method and the largest zone of inhibition was found in the ZnO-20 sample at 8.3 mm. Keywords: ZnO, guava leaf extract, XRD, SEM, antibacterial

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S2 Magister Ilmu Fisika
Pengguna Deposit:	. . Yulianti
Date Deposited:	07 May 2025 02:41
Terakhir diubah:	07 May 2025 02:41
URI:	http://digilib.unila.ac.id/id/eprint/86705

Actions (login required)

Lihat Karya Akhir