PENGARUH PEMANASAN TERHADAP SIFAT MEKANIS (KUAT TARIK) PADA SERAT DAUN NANAS DENGAN MATRIK POLYESTER DARI PT GREAT GIANT PINEAPLE

Erlinda, Maelani (2025) PENGARUH PEMANASAN TERHADAP SIFAT MEKANIS (KUAT TARIK) PADA SERAT DAUN NANAS DENGAN MATRIK POLYESTER DARI PT GREAT GIANT PINEAPLE. Matematika dan Ilmu Pengetahuan Alam, Universitas Lampung.

Preview	File PDF (ABSTRAK) ABSTRAK.pdf Download (194Kb) | Preview
	File PDF (SKRIPSI FULL) SKRIPSI FULL.pdf Restricted to Hanya staf Download (2958Kb)
Preview	File PDF (SKRIPSI TANPA PEMBAHASAN FULL) SKRIPSI TANPA PEMBAHASAN_.pdf Download (2536Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian pengaruh pemanasan terhadap sifat mekanis (kuat tarik) pada serat daun nanas dengan matrik polyester dari PT Great Giant Pineaple yang bertujuan untuk mengetahui pengaruh temperatur terhadap sifat mekanis serat daun nanas dari PT Great Giant Pineaple dalam matriks polyester untuk meningkatkan kekuatan serat daun nanas dan mengetahui morfologi serat daun nanas matriks polyester. Nilai kuat tarik pada kondisi tanpa serat mendapatkan nilai sebesar 0,52 MPa dan tanpa suhu mendapatkan nilai 0,56 MPa relatif rendah. Pada suhu 35℃ mendapatkan nilai sebesar 1,26 MPa pada suhu ini terjadi peningkatan adhesi antara serat dan matriks. Sedangkan pada suhu 40℃ hasil kuat tarik menurun menjadi 0,72 MPa ini disebabkan karena degredasi termal yang mulai terjadi pada suhu yang tinggi. Pada suhu 45℃ mendapatkan hasil kuat tarik turun lebih jauh menjadi 0,47 MPa hal ini disebabkan overheating yang terjadi pada suhu tinggi. Karakterisasi SEM serat daun nanas dalam matriks polyester pada suhu 35℃ menunjukkan distibusi homogen dengan fiber bundles dan permukaan berpori tang mendukung penyerapan resin, meskipun terdapat void yang menjadi potensi kelemahan. Analisis mikroskop optik menunjukkan struktur beraturan dengan retakan kecil akibat perlakuan panas sedangkan sampel tanpa perlakuan panas lebih utuh. The research has been conducted on the effect of heating on mechanical properties (tensile strength) of pineapple leaf fibre with polyester matrix from PT Great Giant Pineaple which aims to determine the effect of temperature on the mechanical properties of pineapple leaf fibre from PT Great Giant Pineaple in polyester matrix to increase the strength of pineapple leaf fibre and determine the morphology of pineapple leaf fibre polyester matrix. The tensile strength value in conditions without fibre gets a value of 0.52 MPa and without temperature gets a value of 0.56 MPa relatively low. At a temperature of 35 ℃, the value is 1.26 MPa at this temperature there is an increase in adhesion between fibre and matrix. While at 40 ℃ the tensile strength results decreased to 0.72 MPa this is due to thermal degredation which began to occur at high temperatures. At 45℃, the tensile strength decreased further to 0.47 MPa due to overheating that occurs at high temperatures. SEM characterisation of pineapple leaf fibres in polyester matrix at 35℃ showed homogeneous distribution with fibre bundles and a porous surface supporting resin absorption, although voids were found to be a potential weakness. Optical microscopy analysis showed a regular structure with small cracks due to heat treatment while the sample without heat treatment was more intact.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika 500 ilmu pengetahuan alam dan matematika > 580 Tumbuh-tumbuhan, tanaman, botani, flora
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Fisika
Pengguna Deposit:	2506661071 Digilib
Date Deposited:	19 Jun 2025 14:13
Terakhir diubah:	19 Jun 2025 14:13
URI:	http://digilib.unila.ac.id/id/eprint/89090

Actions (login required)

Lihat Karya Akhir