KONVERSI MINYAK KELAPA SAWIT MENJADI SENYAWA NITROGEN MENGGUNAKAN ZEOLIT-Y TERPROTONASI SEBAGAI KATALIS DAN UJI AKTIVITAS INHIBITOR KOROSI

Melissa, Putri (2025) KONVERSI MINYAK KELAPA SAWIT MENJADI SENYAWA NITROGEN MENGGUNAKAN ZEOLIT-Y TERPROTONASI SEBAGAI KATALIS DAN UJI AKTIVITAS INHIBITOR KOROSI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK - Melissa Putri.pdf Download (4Mb) | Preview
	File PDF SKRIPSI FULL - Melissa Putri.pdf Restricted to Hanya staf Download (4Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN-1 - Melissa Putri.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Korosi pada baja lunak merupakan masalah di industri, khususnya industri minyak bumi dan gas karena dapat menyebabkan kerusakan material dan kerugian ekonomi, sehingga perlu diatasi menggunakan inhibitor korosi yang ramah lingkungan dan efisien. Penelitian ini bertujuan untuk mensintesis inhibitor korosi berbasis minyak kelapa sawit melalui reaksi dua tahap yaitu transesterifikasi dan amidasi menggunakan katalis zeolit-Y dan zeolit-Y terprotonasi (H-Y) serta uji aktivitas sebagai inhibitor korosi pada baja lunak dalam medium korosif jenuh CO2. Zeolit-Y disintesis dari silika sekam padi melalui metode hidrotermal dan dikarakterisasi menggunakan X-Ray Diffraction (XRD) dan Scanning Electron Microscopy (SEM). Hasil XRD menunjukkan bahwa zeolit-Y yang terbentuk sesuai dengan standar IZA dan hasil SEM menunjukkan bentuk kristal kubik oktahedral. Zeolit-Y diprotonasi menggunakan larutan NH4NO3 3,5 M melalui metode ion exchange untuk menghasilkan zeolit H-Y dan dikarakterisasi menggunakan X-Ray Fluorescence (XRF) menghasilkan konversi Na menjadi H sebesar 65,50%. Reaksi transesterifikasi minyak kelapa sawit dan metanol menggunakan kedua katalis menghasilkan metil ester dengan konversi tertinggi sebesar 32% (H-Y). Metil ester yang diperoleh direaksikan dengan dietanolamina menggunakan katalis yang sama dan selanjutnya dianalisis menggunakan Gas Chromatography-Mass Spectrometry (GC-MS) menghasilkan senyawa nitrogen sebesar 99,10% (H-Y). Senyawa nitrogen yang diperoleh diuji aktivitasnya sebagai inhibitor korosi baja lunak dalam larutan NaCl 3% yang jenuh CO2 menggunakan metode wheel test menunjukkan persen proteksi sebesar 98,17%. Hasil ini didukung oleh data SEM yang menunjukkan morfologi permukaan baja lunak dengan adanya inhibitor korosi terlindungi dengan baik dibandingkan dengan tanpa inhibitor korosi. Kata kunci: inhibitor korosi, senyawa nitrogen, minyak kelapa sawit, zeolit-Y terprotonasi. Corrosion of mild steel is a problem in industry, especially the oil and gas industry because it can cause material damage and economic losses, so it needs to be overcome using environmentally friendly and efficient corrosion inhibitors.This study aims to synthesize palm oil-based corrosion inhibitors through two stage reactions, namely transesterification and amidation using two catalysts namely zeolite-Y and protonated zeolite-Y (H-Y) as well as test activity as corrosion inhibitor on mild steel in a CO2 saturated corrosive medium. Zeolite-Y was synthesized from rice husk silica through hydrothermal method and characterized using X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM).The XRD result showed that the formed zeolite-Y complies with the IZA standard and the SEM result showed an cubic octahedral crystal form. Zeolite-Y was protonated using 3.5 M NH4NO3 solution by ion exchange method to produce zeolite H-Y and characterized using X-Ray Fluorescence (XRF) resulting in a conversion of Na to H of 65.50%. The transesterification reaction of palm oil and methanol using both catalysts produced methyl ester with the highest conversion of 32% by using zeolite H-Y.The obtained methyl ester was reacted with diethanolamine using the same catalyst and then analyzed using Gas Chromatography-Mass Spectrometry (GC- MS) to produce a nitrogen compound of 99.10% (H-Y). The obtained nitrogen compounds were tested for their activities of mild steel corrosion inhibitors in a 3% NaCl solution saturated with CO2 using the wheel test method, showing the best percentage of protection was 98.17%.This result was supported by SEM data which showed that the surface morphology of mild steel with the presence of corrosion inhibitor was well protected compared to without corrosion inhibitor. Keywords: corrosion inhibitor, nitrogen compounds, palm oil, protonated zeolite-Y.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia
Pengguna Deposit:	. . Yulianti
Date Deposited:	24 Oct 2025 08:07
Terakhir diubah:	24 Oct 2025 08:07
URI:	http://digilib.unila.ac.id/id/eprint/91938

Actions (login required)

Lihat Karya Akhir