PENGGUNAAN ZEOLIT-X HASIL MODIFIKASI BENTONIT SEBAGAI KATALIS PADA PROSES PIROLISIS MINYAK KELAPA SAWIT MENJADI BIO CRUDE OIL (BCO)

Erwanda , Lili Utari (2025) PENGGUNAAN ZEOLIT-X HASIL MODIFIKASI BENTONIT SEBAGAI KATALIS PADA PROSES PIROLISIS MINYAK KELAPA SAWIT MENJADI BIO CRUDE OIL (BCO). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Erwanda Lili Utari.pdf Download (12Kb) | Preview
	File PDF SKRIPSI FULL - Erwanda Lili Utari.pdf Restricted to Hanya staf Download (2753Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN - Erwanda Lili Utari.pdf Download (2754Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Biohidrokarbon merupakan salah satu bentuk energi terbarukan yang sedang dikembangkan secara luas sebagai biofuel generasi kedua. Energi ini dapat dihasilkan dari minyak nabati menjadikannya sebagai alternatif energi yang ramah lingkungan dan berkelanjutan. Penelitian ini bertujuan untuk menghasilkan Bio Crude Oil (BCO) melalui proses pirolisis minyak kelapa sawit menggunakan katalis zeolit-X termodifikasi bentonit. Kemudian zeolit-X disintesis dari bentonit dengan menggunakan alumunium foil. Purifikasi bentonit menggunakan larutan HCl 1M, kemudian dikarakterisasi dengan metode X-Ray Flouresence, X-Ray Difraction, dan Scanning Electron Microscope. Hasil analisis XRF menunjukkan bahwa rasio Si/Al mengalami peningkatan bentonit setelah proses purifikasi. Selain itu, berkurangnya kandungan Fe setelah perlakuan asam menunjukkan bahwa logam pengotor berhasil di kurangi. Karakterisasi XRD menunjukkan bahwa bentonit memiliki campuran fasa kristalin dan amorf yang ditandai dengan keberadaan mineral monmorilonit dan kuarsa. Hasil pengamatan SEM menunjukkan, partikel permukaan sebelum pemurnian cenderung menggumpal dan padat, dan tidak teratur tidak homogen. Setelah pemurnian permukaan partikel menjadi lebih terstruktur dan tersebar merata menunjukkan peningkatan kualitas morfologi. Zeolit-X disintesis menggunakan metode hidrotermal dengan variasi waktu kristalisasi 72, 96, dan 120 jam. Hasil terbaik diperoleh pada 72 jam, dibuktikan dengan kesesuaian pola difaktogram terhadap standar Internasional Zeolit Association. Morfologi hasil sintesis menunjukkan struktur tetrahedral khas untuk zeolit-X meskipun masih ada kandungan sodalit pada katalis sampel digunakan dalam proses pirolisis minyak kelapa sawit dengan pemanasan awal 0 hingga 40 menit. Berdasarkan analisis Gas Cromatography-Mass Spectrometry produk BCO terbaik yang diperoleh pada waktu pemanasan 10 menit hidrokarbon sebesar 78,72%. Kata kunci: Bentonit, katalis zeolit-X, minyak kelapa sawit, pirolisis, bio crude oil (BCO). Biohydrocarbons are a form of renewable energy that is being widely developed as a second-generation biofuel. This energy can be produced from vegetable oils making it an environmentally friendly and sustainable energy alternative. This research aims to produce Bio Crude Oil (BCO) through palm oil pyrolysis process using bentonite modified zeolite-X catalyst. Then zeolite-X was synthesized from bentonite using aluminum foil. Purification of bentonite using 1M HCl solution, then characterized by X-Ray Flouresence, X-Ray Diffraction, and Scanning Electron Microscope methods. The results of XRF analysis showed that the Si/Al ratio increased in bentonite after the purification process. In addition, the reduced Fe content after acid treatment showed that the impurity metal was successfully reduced. XRD characterization shows that bentonite has a mixture of crystalline and amorphous phases characterized by the presence of monmorillonite and quartz minerals. SEM observation results show that the surface particles before purification tend to be lumpy and dense, irregular and inhomogens. After purification, the surface particles became more structured and evenly dispersed, indicating an improvement in morphological quality. Zeolite-X was synthesized using hydrothermal method with crystallization time variation of 72, 96, and 120 hours. The best results were obtained at 72 hours, as evidenced by the conformity of the difractogram pattern to the International Zeolite Association standard. The morphology of the synthesized results showed a typical tetrahedral structure for zeolite-X although there was still sodalite content in the catalyst samples used in the pyrolysis process of palm oil with 0 to 40 minutes preheating. Based on Gas Cromatography-Mass Spectrometry analysis the best BCO product obtained at 10 min heating time hydrocarbon amounted to 78.72%. Keywords: Bentonite, zeolite-X catalyst, palm oil, pyrolysis, bio crude oil (BCO).

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia
Pengguna Deposit:	. . Yulianti
Date Deposited:	13 Nov 2025 08:00
Terakhir diubah:	13 Nov 2025 08:00
URI:	http://digilib.unila.ac.id/id/eprint/93264