PROSES PELAPISAN CELUP PADA PLAT BAJA GALVANIS MENGGUNAKAN BAHAN PELAPIS BASAL 250 MESH DAN POLIMER DAMAR SEBAGAI INHIBITOR UNTUK MENINGKATKAN KETAHANAN KOROSI

KHOIROTUL , MUDRIKATU SILFI (2025) PROSES PELAPISAN CELUP PADA PLAT BAJA GALVANIS MENGGUNAKAN BAHAN PELAPIS BASAL 250 MESH DAN POLIMER DAMAR SEBAGAI INHIBITOR UNTUK MENINGKATKAN KETAHANAN KOROSI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF Khoirotul Mudrikatu Silfi_Abstrak - Khoirotul Mudrikatu Silfi.pdf Download (10Kb) | Preview
	File PDF Khoirotul Mudrikatu Silfi_Skripsi Full - Khoirotul Mudrikatu Silfi.pdf Restricted to Hanya staf Download (2376Kb) | Minta salinan
Preview	File PDF Khoirotul Mudrikatu Silfi_Skripsi Tanpa Pembahasan - Khoirotul Mudrikatu Silfi.pdf Download (709Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian proses pelapisan celup pada plat baja galvanis. Pelapisan menggunakan bahan pelapis basal 250 mesh dan ditambah inhibitor polimer damar untuk meningkatkan ketahanan korosi. Penelitian ini bertujuan untuk mengetahui efektivitas pelapisan bubuk basal 250 mesh dalam mencegah korosi pada plat baja galvanis, serta menganalisis pengaruh pemanasan terhadap peningkatan kekerasan plat baja galvanis. Sampel baja galvanis diberi perlakuan panas (furnace) pada suhu 400, 500 dan 600°C dengan waktu pemanasan selama 30 dan 60 menit sebelum dilakukan proses pelapisan. Pengujian laju korosi dilakukan dengan cara direndam menggunakan larutan NaCl 2% dan HCl 2% selama 24, 48, 96, 120 hingga 144 jam untuk mengamati laju korosi. Pelapisan berbahan basal 250 mesh dan perlakuan panas efektif menurunkan laju korosi pada plat baja galvanis. Perlakuan panas menurunkan kekerasan plat baja, di mana baja galvanis tanpa pemanasan memiliki nilai kekerasan lebih tinggi yaitu ASN sebesar 0,80 GPa dan BSH sebesar 1,10 GPa. Uji kekerasan dan ketebalan pelapis juga dilakukan untuk menilai kualitas pelapisan. Karakterisasi dilakukan menggunakan Scanning Electron Microscope- Energy Dispersive X-Ray (SEM-EDX) dan X-Ray Fluorescence (XRF) untuk menganalisis morfologi dan komposisi unsur pada sampel. Hasil penelitian menunjukkan bahwa pelapisan dengan basal mampu meningkatkan ketahanan korosi namun pemanasan plat baja dapat menurunkan kekerasan plat baja galvanis. Kata Kunci: baja galvanis, basal, korosi, uji kekerasan, uji ketebalan. A study on the dip coating process of galvanized steel plates has been conducted. The coating used 250 mesh basalt powder combined with a damar polymer inhibitor to enhance corrosion resistance. This research aims to evaluate the effectiveness of the 250-mesh basalt powder coating in preventing corrosion on galvanized steel plates, as well as to analyse the effect of heat treatment on the hardness improvement of the galvanized steel. Galvanized steel samples were heat treated (furnace) at temperatures of 400, 500 and 600°C with heating times of 30 and 60 minutes before the coating process. Corrosion testing was performed by immersing the samples in 2% NaCl and 2% HCl solutions for 24, 48, 96, 120, and 144 hours to observe the corrosion rate. The results showed that both the basalt coating and the heat treatment effectively reduced the corrosion rate on the galvanized steel plates. Heat treatment reduces the hardness of the steel plate, where galvanized steel without heating has a higher hardness value, namely ASN of 0.80 GPa and BSH of 1.10 GPa. Hardness and coating thickness tests were also carried out to assess the quality of the coating. Characterization was carried out using Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX) and X-Ray Fluorescence (XRF) to analyse the morphology and elemental composition on the sample. The results showed that coating with basalt was able to improve corrosion resistance; however, heating the steel plate reduced the hardness of the galvanized steel. Keywords: galvanized steel, basal, corrosion, hardness test, thickness test.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Fisika
Pengguna Deposit:	A.Md Cahya Anima Putra .
Date Deposited:	29 Jan 2026 07:42
Terakhir diubah:	29 Jan 2026 07:42
URI:	http://digilib.unila.ac.id/id/eprint/95259

Actions (login required)

Lihat Karya Akhir