The repository administrator has not yet configured an RDF license.
PENGEMBANGAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI DENGAN METODE ELEKTROKIMIA DAN APLIKASINYA SEBAGAI KATALIS UNTUK PERENGKAHAN MINYAK NABATI SECARA PIROLISIS
Dalam penelitian ini dipelajari proses pembuatan zeolit sintetik berbasis silika sekam padi dengan metode elektrokimia dan aplikasinya sebagai katalis untuk perengkahan minyak nabati secara pirolisis. Untuk mendapatkan zeolit dengan komposisi yang berbeda, proses elektrokimia dilakukan pada pH yang berbeda, yakni 4, 6, 8, 10, dan potensial yang berbeda, yakni 4, 6, 8 dan 10 volt. Prekursor zeolit yang dihasilkan selanjutnya dikalsinasi pada suhu 300 dan 500 oC, sebelum dicobakan pada perengkahan minyak kelapa dan minyak jarak. Liquid fuel yang dihasilkan dianalisis dengan metode GC-MS untuk mengidentifikasi komponen hasil perengkahan minyak nabati yang dijadikan sampel. Hasil penelitian menunjukkan bahwa katalis yang memiliki unjuk kerja terbaik untuk pirolisis minyak kelapa adalah sampel yang dibuat dengan pH= 4 potensial 8 volt (Zeo4:8) yang dikalsinasi pada suhu 300 oC, menghasilkan liquid fuel dengan kandungan hidrokarbon sebesar 42,06%, sementara untuk minyak jarak katalis yang terbaik adalah Zeo4:10 yang dikalsinasi pada suhu 300 oC menghasilkan liquid fuel dengan kandungan hidrokarbon sebesar 63,06%, dan Zeo4:4 yang dikalsinasi pada suhu 500 oC menghasilkan liquid fuel dengan kandungan hidrokarbon sebesar 78,28%. Karakterisasi menggunakan XRD menunjukkan bahwa sampel masih didominasi struktur amorf, dan adanya fasa albite dan nepheline, yang menunjukkan bahwa sampel belum sepenuhnya berubah menjadi zeolit, sehingga sampel masih dianggap sebagai prekursor zeolit. Karakterisasi menggunakan SEM menunjukkan bahwa sampel memiliki morfologi permukaan yang homogen, dan karakterisasi dengan EDS menunjukkan unsur kimia pembentuk zeolit, yang menunjukkan bahwa metode elektrokimia dapat digunakan sebagai alternatif untuk menghasilkan prekursor zeolit sintetik. Kata kunci : silika sekam padi, zeolit sintetik, metode elektrokimia, pirolisis, liquid fuel DEVELOPMENT OF SYNTHETIC ZEOLITES FROM RICE HUSK SILICA USING ELECTROCHEMICAL METHOD AND APPLICATION AS CATALYST FOR PYROLYTIC CRACKING OF VEGETABLE OILS In this research, a series of synthetic zeolites was prepared from rice husk silica using electrochemical method. The zeolites were subsequently tested as catalysts for pyrolytic cracking of vegetable oils. To produce zeolites with varied compositions, preparation was carreid out by applying different pHs and potentials. Before use, then catalysts were subjected to calcination treatments at different temperatures of 300 and 500 °C, and the liquid fuels produced were analyzed by GC-MS to identify the components of the liquid fuels. The results showed that the zeolites having the best performance for the pyrolysis of the coconut oil was the zeolite synthesized at pH = 4 and potential of 8 volt (Zeo4: 8) which was calcinated at 300 °C and producing the liquid fuel with hydrocarbon content of 42.06%, while for castor oil, the best catalyst was Zeo4: 10 calcinated at 300 °C producing liquid fuel with hydrocarbon content of 63.06%. The Zeo4: 4 calcinated at 500 °C was found to produce liquid fuel with hydrocarbon content of 78.28%. The characterization by XRD showed that complete conversion of the samples into zeolite has not been achieved, and therefore they are considered as zeolite precursors. It is also found that according to SEM, the surface of the samples is characterized by relatively homogeneous morphology, while the EDS results confirmed the elemental composition of the samples is in accordance with that of zeolite. Keywords: rice husk silica, synthetic zeolite, electrochemical method, pyrolysis, liquid fuel
PENGEMBANGAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI DENGAN METODE ELEKTROKIMIA DAN APLIKASINYA SEBAGAI KATALIS UNTUK PERENGKAHAN MINYAK NABATI SECARA PIROLISIS (File PDF)
PENGEMBANGAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI DENGAN METODE ELEKTROKIMIA DAN APLIKASINYA SEBAGAI KATALIS UNTUK PERENGKAHAN MINYAK NABATI SECARA PIROLISIS (Other)
HTML Summary of #11114 PENGEMBANGAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI DENGAN METODE ELEKTROKIMIA DAN APLIKASINYA SEBAGAI KATALIS UNTUK PERENGKAHAN MINYAK NABATI SECARA PIROLISIS
QD Chemistry