%T FABRIKASI DAN KARAKTERISASI KERAMIK KALSIUM ALUMINAT  MENGGUNAKAN BAHAN DASAR KALSIUM KARBONAT DARI  CANGKANG TELUR DAN ALUMINA KOMERSIAL DENGAN  METODE REAKSI PADATAN
%U http://digilib.unila.ac.id/13304/
%X Abstrak    Telah dilakukan fabrikasi dan karakterisasi keramik kalsium aluminat  menggunakan bahan dasar kalsium karbonat dari cangkang telur dan alumina  komersial dengan metode reaksi padatan. Hasil karakterisasi XRD menunjukkan  fasa yang terbentuk adalah corundum, grossite dan calcium aluminum oxide.  Hasil karakterisasi SEM menunjukkan mikrostruktur butiran partikel yang  terbentuk sudah terlihat jelas, pori-pori semakin berkurang dan lebih homogen.  Hasil karakterisasi FTIR menunjukkan ikatan yang terbentuk adalah Ca-O, Al-O  dan OH. Hasil karakterisasi sifat fisis menunjukkan bahwa semakin tinggi suhu  sintering maka nilai densitas, penyusutan dan resistivitas sampel kalsium aluminat  akan semakin meningkat. Namun nilai porositas sampel kalsium aluminat  menurun, hal ini dikarenakan semakin tinggi suhu sintering maka kerapatan  butiran-butiran semakin meningkat.  Kata kunci: kalsium aluminat, reaksi padatan, XRD, SEM, FTIR, sifat fisis.    Abstract    In this research fabrication and characterization of calcium aluminate ceramics by  using raw material of egg shell and alumina commercial with a solid state reaction  technique was done. XRD characterization result showed that the formation of  calcium aluminate phase is formed corundum, grossite and calcium aluminum  oxide. SEM characterization result showed that grain boundaries disappeared,  pores that became small and homogeneous. FTIR characterization result showed  that the functional group is formed Ca-O, Al-O and OH. Then evaluation of  physical properties showed that if heating temperature that was applied in the  sample was higher, it causes density, shrinkage and resistivity will be more  increases where as the porosity of the sample decrease.  Key words: calcium aluminate, solid state reaction, FTIR, SEM, XRD, physical  properties.