TY  - GEN
ID  - eprints13304
UR  - http://digilib.unila.ac.id/13304/
A1  - 0717041019,  ADE FATHUROHMAN
Y1  - 2012/02/03/
N2  - Abstrak

Telah dilakukan fabrikasi dan karakterisasi keramik kalsium aluminat
menggunakan bahan dasar kalsium karbonat dari cangkang telur dan alumina
komersial dengan metode reaksi padatan. Hasil karakterisasi XRD menunjukkan
fasa yang terbentuk adalah corundum, grossite dan calcium aluminum oxide.
Hasil karakterisasi SEM menunjukkan mikrostruktur butiran partikel yang
terbentuk sudah terlihat jelas, pori-pori semakin berkurang dan lebih homogen.
Hasil karakterisasi FTIR menunjukkan ikatan yang terbentuk adalah Ca-O, Al-O
dan OH. Hasil karakterisasi sifat fisis menunjukkan bahwa semakin tinggi suhu
sintering maka nilai densitas, penyusutan dan resistivitas sampel kalsium aluminat
akan semakin meningkat. Namun nilai porositas sampel kalsium aluminat
menurun, hal ini dikarenakan semakin tinggi suhu sintering maka kerapatan
butiran-butiran semakin meningkat.
Kata kunci: kalsium aluminat, reaksi padatan, XRD, SEM, FTIR, sifat fisis.

Abstract

In this research fabrication and characterization of calcium aluminate ceramics by
using raw material of egg shell and alumina commercial with a solid state reaction
technique was done. XRD characterization result showed that the formation of
calcium aluminate phase is formed corundum, grossite and calcium aluminum
oxide. SEM characterization result showed that grain boundaries disappeared,
pores that became small and homogeneous. FTIR characterization result showed
that the functional group is formed Ca-O, Al-O and OH. Then evaluation of
physical properties showed that if heating temperature that was applied in the
sample was higher, it causes density, shrinkage and resistivity will be more
increases where as the porosity of the sample decrease.
Key words: calcium aluminate, solid state reaction, FTIR, SEM, XRD, physical
properties.
TI  - FABRIKASI DAN KARAKTERISASI KERAMIK KALSIUM ALUMINAT
MENGGUNAKAN BAHAN DASAR KALSIUM KARBONAT DARI
CANGKANG TELUR DAN ALUMINA KOMERSIAL DENGAN
METODE REAKSI PADATAN
AV  - restricted
ER  -