        abstract = {The reaserch on the synthesis, characterization, and application of organotin (IV)
4-aminobenzoate derivative compounds as corrosion inhibitor on mild steel type
HRP (Hot Roller Plate) in DMSO-HCl corrosive medium has been performed.
Diphenyltin(IV) di-4-aminobenzoate and dibutyltin(IV) di-4-aminobenzoate
compound have successfully been synthesized. The synthesized compounds were
characterized using IR spectrophotometry, UV, NMR, and microelemental
analyzer and the activity anticorrosion test was carried using the EA10
potentiostat. The surface analysis of mild steel was performed using a trinoculer
microscope. Based on the result of characterization, it has been shown that
diphenyltin(IV) di-4-aminobenzoate and dibutytin(IV) di-4-aminobenzoate
compound have successfully been synthesized with the presence of functional
groups, {\ensuremath{\lambda}}max, and the composition of the element as expected. Diphenyltin(IV) di-
4-aminobenzoate compound was found as a white solid product with a yield of
93.16\% and dibutyltin(IV) di-4-aminobenzoate compound as a whitish yellow
product with a yield of 87.47\%. The results of anticorrosion test showed that the
highest inhibiton activity was at concentration of 100 mg / L both compounds
tested with the precentage of inhibition efficiency were 40.54 and 37.5\%,
respectively.
Keyword : corrosion inhibition activity, dibutyltin(IV) di 4-aminobenzoate,
diphenyltin(IV) di-4-aminobenzoate

Telah dilakukan penelitian mengenai sintesis, karakterisasi, dan aplikasi turunan
senyawa organotimah(IV) 4-aminobenzoat sebagai inhibitor korosi pada baja
lunak tipe HRP (Hot Roller Plat) dalam medium korosif DMSO-HCl. Dilakukan
sintesis senyawa difeniltimah(IV) di-4-aminobenzoat dan dibutiltimah(IV) di-4-
aminobenzoat. Senyawa hasil sintesis dikarakterisasi menggunakan
spektrofotometri IR, UV, NMR, dan microelemental analyzer serta pengujian
aktivitas antikorosi menggunakan potensiostat EA10. Analisis permukaan baja
dilakukan dengan menggunakan mikroskop Trinokuler. Dari hasil karakterisasi
dapat diketahui bahwa senyawa difeniltimah(IV) di-4-aminobenzoat dan
dibutiltimah(IV) di-4-aminobenzoat telah berhasil disintesis dengan adanya
gugus-gugus fungsi, {\ensuremath{\lambda}}max, dan komposisi unsur dari senyawa yang diharapkan.
Senyawa difeniltimah(IV) di-4-aminobenzoat berupa padatan putih keruh dengan
rendemen senyawa 93,16 \% dan senyawa dibutiltimah(IV) di-4-aminobenzoat
berupa padatan berwarna kuning keputihan dengan rendemen senyawa 87,47 \%.
Hasil pengujian aktivitas antikorosi menunjukkan penghambatan tertinggi
masing-masing terjadi pada konsentrasi 100 mg/L oleh senyawa difeniltimah(IV)
di-4-aminobenzoat dan senyawa dibutiltimah(IV) di-4-aminobenzoat dengan
persen efisiensi inhibisi masing-masing sebesar 40,54 dan 37,5 \%.
Kata kunci : aktivitas inhibisi korosi, dibutiltimah(IV) di-4-aminobenzoat,
difeniltimah(IV) di-4-aminobenzoat.}
}