%0 Journal Article
%A 0817041014, Adelina S.E Sianturi
%D 2012
%F eprints:14347
%J Digital Library
%T PENGARUH VARIASI SUHU PEMANASAN  DENGAN PENDINGINAN SECARA  LAMBAT TERHADAP UJI BENDING DAN  STRUKTUR MIKRO PADA BAJA PEGAS  DAUN AISI 5140
%U http://digilib.unila.ac.id/14347/
%X Abstrak    Telah dilakukan penelitian tentang pengaruh variasi suhu pemanasan dan  pendinginan secara lambat terhadap uji bending dan struktur mikro pada baja  pegas daun AISI 5140. Penelitian ini dilakukan untuk mengetahui komposisi  kimia, struktur mikro dan keuletan baja pegas daun AISI 5140. Proses heat  treatment diberikan dengan variasi suhu pemanasan 750 oC, 800 oC dan 880 oC  dengan holding time 60 menit kemudian didinginkan secara lambat. Uji komposisi  kimia baja pegas daun AISI 5140 masuk kategori baja karbon sedang (0,42177  %C). Pada uji bending bahwa dengan proses pendinginan secara lambat  menghasilkan baja dengan tingkat keuletan yang semakin tinggi tetapi semakin  besar suhu austenisasinya maka tingkat kekuatan menahan beban semakin tinggi  dan keuletannya semakin menurun. Dari hasil struktur mikro sampel baja pegas  daun dengan pendinginan secara lambat menghasilkan butir-butir ferit dan perlit  sedangkan pada baja yang original menghasilkan butir-butir martensit dan perlit  dimana butir-butir perlit yang terlihat sangat halus dan sedikit dibanding fasa  martensit.  Kata kunci: Baja pegas daun, proses heat treatment, pendinginan secara lambat  (annealing), uji bending, struktur mikro.                Abstract    A study was done concerning the effect of temperatures variations heating with  annealing toward bending test and micro structure in leaf springs steel AISI 5140.  The study was conducted to determine the chemical composition, microstructure  and toughness leaf spring steel AISI 5140. The process of heat treatment was  given temperatures variation heating 750 °C, 800 °C and 880 °C with holding  time of 60 minutes and then cooled slowly. Test the chemical composition of leaf  springs steel AISI 5140 included the category of medium carbon steel (0.42177%  C). In the bending test with annealing process produced steels with higher levels  of austenite ductility temperature but the greater level of the higher loaded the  bearing strength and the tenacity decreased. The results of the micro structure  sample of leaf spring steel with annealing, it produced grains of ferrite and  pearlite, while the original steel was producing grains of martensite and pearlite  pearlite grains which looked very smooth and less than the martensite phase.  Key words: leaf spring steel, heat treatment process, annealing, bending test,  micro structure.  .