%0 Journal Article
%A 0717041056, PASCOLI HANES
%D 2012
%F eprints:14586
%J Digital Library
%T PEMBUATAN NANOKOMPOSIT TITANIA-SILIKA DARI BAHAN  TITANIUM TRIKLORIDA (TiCl3) DAN SILIKA SEKAM PADI DENGAN  METODE SOL-GEL
%U http://digilib.unila.ac.id/14586/
%X Abstrak    Telah dilakukan sintesis dan karakterisasi nanotitania (TiO2) dan nanokomposit  titania-silika (TiO2-SiO2) dengan metode sol-gel antara campuran titanium  triklorida (TiCl3) dan silika sekam padi. Desain mikrostruktur dilakukan dengan  variasi waktu proses sol-gel pada sekitar 3, 5, 7, 9, 11, dan 13 jam. Karakterisasi  dilakukan dengan difraksi sinar-X (XRD), scanning electron microscopy (SEM),  dan metode empat titik. Struktur titania yang diperoleh adalah anatase yang masih  didominasi fasa amorf dan struktur komposit titania-silika berfasa amorf  sebagaimana sampel hanya dikalsinasi pada temperatur 550oC. Mikrostruktur  nanotitania dan nanokomposit tiania-silika semakin homogen seiring dengan  lamanya proses. Hal ini serupa pada nilai resistivitas nanokomposit titania-silika.  Nilai resistivitas berkurang dengan meningkatnya proses waktu sol-gel. Dalam  proses sol-gel, efek dari dinamika Brown dapat memperoleh diameter butiran  nanokomposit titania-silika berkisar 60-100 nm sebagaimana dipastikan dari hasil  SEM. Hasil EDS menunjukkan perbandingan persentase massa pada titania dan  silika dalam komposit adalah 31,68 dan 68,32%.  Kata Kunci: nanokomposit titania-silika, sekam padi, sol-gel, mikrostruktur,  resistivitas.        Abstract    Synthesis and characterization nanotitania and nanocomposite titania-silica (TiO2-  SiO2) was carried out with sol-gel method from mixture of titanium trichloride  and silica from rice husk. Microstructural design was conducted by the various of  the sol-gel process at about 3, 5, 7, 9 11, and 13 hours. The characterization was  done by X-ray diffraction (XRD), scanning electron microscopy (SEM), and four  points method. The structure of titania obtained was anatase which was still  dominated by amorphous phase. The structure of titania-silica composite was  amorphous phase as a sample was only calcined at 500oC. Microstructural  nanotitania and nanocomposite are more homogeneous along with long process.  This is similiar to the trend of resistivity titania-silica nanocomposite.The  resistivity decreased with increased of the time sol-gel process. In sol-gel method,  the effect of Brownian dynamics can gain the grains diameter of titania-silica  composite ranged about 60-100 nm as confirmed by SEM. The EDS shows the  ratio of weight percent for titania and silica in the composite is 31.68 and 68.32%.  Key Word: nanocomposite titania-silica, rice husk, sol-gel, microstructure,  resistivity.