title: PREPARASI DAN KARAKTERISASI KERAMIK SILIKA (SiO2) SEKAM
PADI DENGAN SUHU KALSINASI 800 oC - 1000 oC
ispublished: pub
subjects: QC
full_text_status: restricted
abstract: ABSTRAK
Penelitian ini bertujuan untuk mensistesis keramik silika (SiO2) yang diperoleh
dari sekam padi menggunakan metode leaching dengan asam sitrat (C6H8O7)
yang dikalsinasi pada suhu 800 ºC, 900 ºC, dan 1000 ºC. Sampel yang diperoleh
dikarakterisasi menggunakan Differential Thermal Analysis dan
Thermogravimetric Analysis (DTA/TGA), Fourier Transform Infrared (FTIR), XRay
Diffraction (XRD), dan Scanning Electron Microscopy (SEM). Hasil
karakterisasi DTA menunjukkan sifat termal silika terjadi peristiwa penyerapan
panas (endoterm) yang mengindikasikan adanya polisakarida dipolimerisasi dan
dehidrasi yang masing-masing terletak pada suhu 312 ºC dan 355 ºC. Gugus
fungsi yang terbentuk pada karakterisasi FTIR menunjukkan adanya vibrasi ulur –
OH dari Si-OH, vibrasi tekuk –OH, vibrasi ulur asimetri Si-O dari Si-O-Si,
vibrasi ulur Si-O dari Si-OH, dan vibrasi tekuk Si-O-Si. Gugus fungsi Si-O pada
Si-OH menurun pada bilangan gelombang 812,3 cm-1 dengan naiknya suhu pada
1000 ºC. Karakterisasi XRD menunjukkan bentuk amorf ketika dilakukan
kalsinasi pada suhu 800 ºC dan fasa tridimit pada suhu 900 ºC dan 1000 ºC.
Scanning Electron Microscopy (SEM) menunjukkan luas permukaan dan ukuran
pori yang semakin merapat yang disebabkan terjadinya pengerutan partikel silika
yang dikalsinasi pada suhu pembakaran yang tinggi.
Kata kunci: Asam sitrat, DTA/TGA, FTIR, leaching, sekam padi, SEM, silika dan XRD.
The objective of this research is to synthesize of silica (SiO2) ceramics obtained
from rice husk by using citric acid (C6H8O7) leaching method and calcined at 800
ºC, 900 ºC, and 1000 ºC. The samples obtained were characterized using
Differential Thermal Analysis and Thermogravimetric Analysis (DTA/TGA),
Fourier Transform Infrared (FTIR), X-Ray Diffraction (XRD), and Scanning
Electron Microscopy (SEM). The DTA result showed that thermal properties of
silica events heat absorption (endothermic) which indicates the presence of
polymerized polysaccharide and dehydration are respectively located at a
temperature of 312 ºC and 355 ºC. The functional groups presence in the FTIR
result were -OH stretching vibration of Si-OH, -OH bending vibrations,
asymmetric stretching vibration of Si-O of the Si-O-Si, Si-O stretching vibration
of Si-OH and bending vibrations of Si-O-Si. Si-O functional groups on Si-OH
decreased in wavenumber 812.3 cm-1 with a temperature rise at 1000 ºC. XRD
result showed that at 800 ºC the phase is amorphous, but at 900 ºC and 1000 ºC
the phase present is trydimite. SEM result showed that the surface area and pore
size were getting increasingly closer due to the contraction of the silica particles
in the calcination at high combustion temperatures.
Keywords. Citric acid, DTA/TGA , FTIR , leaching, rice husk, SEM , silica, and
XRD.
date: 2015-12-11
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
place_of_pub: UNIVERSITAS LAMPUNG
institution: UNIVERSITAS LAMPUNG
department: FMIPA
thesis_type: other
citation:   RIEZKA ROSALIA, 0917041047  (2015) PREPARASI DAN KARAKTERISASI KERAMIK SILIKA (SiO2) SEKAM PADI DENGAN SUHU KALSINASI 800 oC - 1000 oC.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/16182/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/16182/1/ABSTRACT.pdf
document_url: http://digilib.unila.ac.id/16182/2/COVER%20DALAM.pdf
document_url: http://digilib.unila.ac.id/16182/3/COVER%20LUAR.pdf
document_url: http://digilib.unila.ac.id/16182/7/KATA%20PENGANTAR.pdf
document_url: http://digilib.unila.ac.id/16182/8/LEMBAR%20PENGESAHAN.pdf
document_url: http://digilib.unila.ac.id/16182/9/LEMBAR%20PERNYATAAN.pdf
document_url: http://digilib.unila.ac.id/16182/10/MOTO.pdf
document_url: http://digilib.unila.ac.id/16182/123/DAFTAR%20ISI.pdf
document_url: http://digilib.unila.ac.id/16182/11/LEMBAR%20PERSETUJUAN.pdf
document_url: http://digilib.unila.ac.id/16182/124/DAFTAR%20TABEL.pdf
document_url: http://digilib.unila.ac.id/16182/13/PERSEMBAHAN.pdf
document_url: http://digilib.unila.ac.id/16182/125/DAFTAR%20GAMBAR.pdf
document_url: http://digilib.unila.ac.id/16182/14/RIWAYAT%20HIDUP.pdf
document_url: http://digilib.unila.ac.id/16182/15/SANWACANA.pdf
document_url: http://digilib.unila.ac.id/16182/16/BAB%20I.pdf
document_url: http://digilib.unila.ac.id/16182/126/BAB%20II.pdf
document_url: http://digilib.unila.ac.id/16182/127/BAB%20III.pdf
document_url: http://digilib.unila.ac.id/16182/128/BAB%20IV.pdf
document_url: http://digilib.unila.ac.id/16182/129/BAB%20V.pdf
document_url: http://digilib.unila.ac.id/16182/130/DAFTAR%20PUSTAKA.pdf