The repository administrator has not yet configured an RDF license.
PENGARUH SEMEN OPC DAN PCC TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON MUTU TINGGI FAKTOR AIR SEMEN 0,30 DAN 0,33
Semen yang biasa digunakan dalam pembuatan beton adalah semen portland type I OPC (Ordinary Portland Cement). Akan tetapi, semen tipe I OPC (Ordinary Portland Cement) tersebut sudah mulai digantikan dengan semen jenis PCC oleh para industri semen di Indonesia. Penelitian ini dilakukan untuk mengetahui pengaruh semen OPC dan PCC terhadap kuat tekan dan kuat lentur pada beton mutu tinggi faktor air semen 0,30 dan 0,33. Benda uji dalam penelitian ini adalah silinder beton dengan diameter 15 cm dan tinggi 30 cm. Dan benda uji balok beton dengan panjang 60 cm, lebar 15 cm dan tinggi 15 cm. Pengujian yang dilakukan yaitu, kuat tekan dan kuat lentur beton mutu tinggi setelah benda uji berumur 14 hari, 28 hari dan 56 hari. Faktor air semen rencana adalah 0,30 dan 0,33. Bahan tambahan yang digunakan yaitu Superplasticizer dan Silica fume. Berdasarkan hasil pengujian kuat ketan beton, kuat tekan rata-rata beton yang dihasilkan tidak mencapai target kuat tekan rencana beton mutu tinggi. Namun pada pengujian kuat lentur beton, kuat lentur beton rata-rata yang dihasilkan memenuhi beton mutu tinggi bila dibandingkan dengan kuat lentur teori. Pada semen PCC nilai kuat tekan rata-rata tertinggi terdapat pada benda uji fas 0,30 degan penambahan 10% Silica fume yaitu berturut-turut sebesar 29,8184 MPa; 30,2902 MPa dan 36,2350 MPa, sedangkan untuk semen OPC didapat pada benda uji fas 0,33 tanpa penambahan Silica fume yaitu berturut-turut sebesar 30,1014 MPa; 34,0646 MPa dan 47,8415 MPa. Nilai kuat lentur rata-rata tertinggi untuk semen PCC terdapat pada benda uji fas 0,30 degan penambahan 10% Silica fume yaitu berturut-turut sebesar 6,7556 MPa; 7,0667 MPa dan 7,4444 MPa, sedangkan untuk semen OPC didapat pada benda uji fas 0,30 tanpa penambahan Silica fume yaitu berturut-turut sebesar 9,0000 MPa; 6,6667 MPa dan 8,3556 MPa. Kata kunci: Semen OPC, Semen PCC, kuat tekan, kuat lentur ABSTRAK BAHASA INGGRIS The cement used in the manufacture of portland cement concrete is a type I OPC (Ordinary Portland Cement). However, cement type I OPC (Ordinary Portland Cement) is already being replaced by cement type of PCC by the cement industry in Indonesia. This study was conducted to determine the effect of OPC cement and PCC of compressive strength and flexural strength at high strength concrete cement water factor of 0,30 and 0,33. The object of this research is a concrete cylinder with a diameter of 15 cm and height 30 cm . And the concrete beam with a length of 60 cm, width 15 cm and height 15 cm. Tests were carried out, namely, compressive strength and flexural strength of high strength concrete after the test specimen was 14 days, 28 days and 56 days. Plant cement factor was 0,30 and 0,33. Additional materials used are superplasticizer and silica fume. Based on test results compressive strength concrete, the average compressive strength of concrete produced does not reach the target compressive strength of high strength concrete plan. However the flexural strength testing of concrete, concrete flexural strength averages produced meet high strenght concrete flexural strength when compared with the theory. At PCC cement compressive strength value of the highest average found in the test object fas 0,30 with addition of 10% Silica fume is of 29,8184 MPa; 30,2902 MPa and 36,2350 MPa, whereas for OPC cement obtained in the test object without adding Silica fume with cement water factor 0,33, the results are 30,1014 MPa; 34,0646 Mpa and 47,8415 MPa. Flexural strength value of the highest average for PCC cement specimen contained in Cement water factor 0,30 with addition of 10% Silica fume, the result are 6,7556 MPa; 7,0667 MPa and 7,4444 MPa, whereas for OPC cement obtain without adding cement water factor 0,30 with Silica fume gets of 9,0000 MPa; 6,6667 MPa and 8,3556 MPa. Keywords: OPC cement, PCC cement, compressive strength, flexural strength
PENGARUH SEMEN OPC DAN PCC TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON MUTU TINGGI FAKTOR AIR SEMEN 0,30 DAN 0,33 (File PDF)
PENGARUH SEMEN OPC DAN PCC TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON MUTU TINGGI FAKTOR AIR SEMEN 0,30 DAN 0,33 (Other)
HTML Summary of #16607 PENGARUH SEMEN OPC DAN PCC TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON MUTU TINGGI FAKTOR AIR SEMEN 0,30 DAN 0,33
Konstruksi bangunan