           title = {PENGOLAHAN KALENG ALUMINIUM BEKAS MENJADI
ALUMINOSILIKAT BERBASIS SILIKA SEKAM PADI DENGAN
METODE ELEKTROKIMIA SEBAGAI KATALIS
TRANSESTERIFIKASI MINYAK BIJI KARET},
          author = {1117011049  UMI FADILAH },
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM },
            year = {2016},
             url = {http://digilib.unila.ac.id/21039/},
        abstract = {Dalam penelitian ini telah dilakukan pembuatan katalis aluminosilikat dari kaleng
aluminium bekas dan sekam padi menggunakan metode elektrokimia. Sintesis
katalis dilakukan dengan elektrolisis kaleng bekas dalam sol silika pada pH 10,0
dengan variasi waktu 1, 2, dan 3 jam pada potensial 8, 10, dan 12 volt.
Aluminosilikat dikalsinasi pada suhu 600 oC selama 4 jam dan digunakan sebagai
katalis dalam reaksi transesterifikasi minyak biji karet. Hasil transesterifikasi
menunjukkan bahwa semua katalis mampu bekerja meskipun dengan rendemen
yang rendah, yakni 24,93-29,39\%. Karakterisasi produk transesterifikasi
menggunakan GC-MS menunjukkan adanya lima metil ester asam lemak dengan
komposisi tertinggi adalah metil linoleat, yakni 36,80\% sesuai dengan asam lemak
yang terkandung dalam minyak biji karet. Katalis dikarakterisasi dengan XRD
menunjukkan bahwa katalis masih berfasa amorf, karakterisasi dengan SEM
menunjukkan bahwa katalis memiliki permukaan berpori dan terdapat cluster
dengan ukuran dan bentuk yang bervariasi selaras dengan hasil karakterisasi
menggunakan PSA. Hasil EDS menunjukkan unsur yang terkandung dalam
sampel adalah O, Si, Al, Na, C, Mg, Mn, Br, dan F dan karakterisasi dengan XRF
menunjukkan bahwa senyawa mayor dalam katalis adalah Al2O3 dan SiO2, dan
beberapa unsur minor yang kemungkinan besar berasal dari kaleng bekas dan
sekam padi.
Kata kunci : Kaleng aluminium bekas, katalis aluminosilikat, metode
elektrokimia, transesterifikasi, minyak biji karet.

ABSTRACT

In this study a series of aluminosilicate catalysts was synthesized from used
aluminum cans and rice husk silica using electrochemical method. Preparation of
the catalysts was carried out by electrolysis of the cans in silica sol at pH 10.0 for
different times of 1, 2, and 3 hours at potential 8, 10, and 12 volt. Aluminosilicate
was calcined at 600 oC for 4 hours and then tested for transesterification of rubber
seed oil. The experimental results showed that all catalysts were able to work
although with a low yield, that is 24.93-29.39\%. Characterization of
transesterification products with GC-MS indicates the presence of five fatty acid
methyl esters with methyl linoleic as the most abundant (36.80\%), in accordance
with the existence of linoleic acid as the main component of the rubber seed oil.
Characterization of catalysts with XRD showed that catalysts still amorphous
phase, with the surface marked with the presence of pores and clusters with
different sizes and shapes based on SEM technique, and in agreement with
particle size distribution as seen by PSA technique. The result of EDS technique
revealed the existence of elements includes O, Si, Al, Na, C, Mg, Mn, Br, and F
and characterization with XRF showed that mayor compounds in the catalysts are
Al2O3 and SiO2, with several minor elements most likely originated from
aluminum cans and rice husk.
Keywords : Aluminum cans, aluminosilicate catalysts, electrochemical method,
transesterification, rubber seed oil.}
}