           title = {PREPARASI DAN KARAKTERISASI LIMBAH BIOMATERIAL
CANGKANG KEONG MAS (Pomacea canaliculata Lamarck) DARI
DAERAH PERINGSEWU SEBAGAI BAHAN DASAR BIOKERAMIK},
          author = {(1117041020) LARAS PANCAWATI },
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM},
            year = {2016},
             url = {http://digilib.unila.ac.id/22128/},
        abstract = {ABSTRAK
Cangkang keong mas (Pomacea canaliculata Lamarck) diketahui banyak
mengandung kalsium karbonat (CaCO3) yang dapat digunakan sebagai sumber
pembuatan biokeramik, yaitu dengan cara mensintesis CaCO3 menjadi CaO pada
suhu tinggi. Cangkang keong mas dicuci, dikeringkan, digerus, lalu dikalsinasi
dalam furnace pada suhu 500 ?C, 800 ?C dan 1000 ?C selama 3 jam dan kalsium
karbonat (CaCO3) komersil digunakan sebagai sampel pembanding. Kemudian
dilakukan karakterisasi Different Thermal Analysis/ Thermogravimetric Analysis
(DTA/TGA) untuk mengetahui perlakuan termal terhadap sampel, X-Ray
Difraction (XRD) untuk mengetahui fasa yang terbentuk, Fourier Transform Infra
Red (FTIR) untuk mengetahui gugus fungsi dan Scanning Electron Microscopy
(SEM) untuk mengetahui morfologi permukaan dan kandungan kimia pada
sampel. Proses kalsinasi menyebabkan dekomposisi CaCO3 menjadi CaO, seperti
hasil XRD yang menunjukkan setelah kalsinasi diatas suhu 800 ?C muncul fasa
CaO dan Ca(OH)2. Hasil EDX menunjukkan bahwa kandungan terbesar pada
cangkang adalah Ca dan CaO.
Kata kunci : Keong mas (Pomacea canaliculata L), kalsinasi, kalsium karbonat
(CaCO3) komersil, kalsium oksida.
ABSTRACT
Snails shell (Pomacea canaliculata Lamarck) known to contain lots of calcium
carbonate (CaCO3) which can be used as source of manufacture bioceramic, that
is by synthesizing CaCO3 became CaO at high temperature. Snails shell washed,
dried, crushed, and then calcination in air at 500 ?C, 800 ?C and 1000 ?C for 3
hours and calcium carbonate (CaCO3) commercial used for comparison. Then
characterization Differential Thermal Analysis / Thermogravimetric Analysis
(DTA/TGA) to explain the effect of calcinations temperature, crystalline phase
formed detected by analyzed X-Ray Difraction (XRD), then functional groups by
analyzed Fourier Transform Infra Red (FTIR) and Scanning Electron Microscopy
(SEM) to observed their surface morphology and chemical compositions. Effect
calcination can be causes decomposition of CaCO3 into CaO, that showed at
analyzed XRD for calcined sampel above 800 ?C appears phase CaO and
Ca(OH)2. EDX results showed that the largest content in snail shell is Ca and
CaO.
Keywords: Snails (Pomacea canaliculata Lamarck), calcination, calcium
carbonate (CaCO3) commercial, calcium oxide.}
}