title: SINTESIS DAN KARAKTERISASI SENYAWA TRIFENILTIMAH(IV)  HIDROKSIBENZOAT SEBAGAI INHIBITOR KOROSI PADA BAJA  LUNAK DALAM DMSO-HCl
creator: MURNI FITRIA,  1217011040
subject: Q Science (General)
description: Telah dilakukan sintesis senyawa trifeniltimah(IV) hidroksibenzoat dengan  mereaksikan ligan 2-hidroksi dan 4-hidroksibenzoat dengan trifeniltimah(IV)  hidroksida dalam larutan metanol. Persen hasil sintesis senyawa trifeniltimah(IV)  2-hidroksibenzoat dan trifeniltimah(IV) 4-hidroksibenzoat adalah 79,77 dan  89,66%. Senyawa tersebut dikarakterisasi menggunakan teknik spektroskopi infra  merah (IR), ultra ungu, dan analisis unsur. Besarnya inhibisi trifeniltimah(IV) 2-  hidroksibenzoat dan trifeniltimah(IV) 4-hidroksibenzoat pada korosi baja lunak  dalam DMSO-HCl dikaji dengan polarisasi potensiodinamik. Hal tersebut  menunjukkan bahwa senyawa trifeniltimah(IV) 2-hidroksibenzoat dan  trifeniltimah(IV) 4-hidroksibenzoat merupakan inhibitor korosi yang bagus untuk  perlindungan baja lunak. Tingginya efisiensi inhibisi berhubungan dengan efek  pengeblokan sederhana melalui adsorpsi molekul inhibitor pada permukaan baja  lunak. Nilai persen efisiensi inhibisi (EI) tertinggi senyawa trifeniltimah(IV) 2-  hidroksibenzoat adalah 58,52 dan trifeniltimah(IV) 4-hidroksibenzoat adalah  61,72% pada konsentrasi 100 ppm.  Kata kunci: trifeniltimah(IV) hidroksibenzoat, potensiodinamik, korosi.    abstract    The synthesis of triphenyltin(IV) hydroxibenzoates were performed by reacting  ligands of 2-hydroxy and 4-hydroxibenzoic acid with triphenyltin(IV) hydroxide  in methanol solution. The percentage yiels of the compounds synthesized  triphenyltin(IV) 2-hydroxibenzoate and triphenyltin(IV) 4-hydroxibenzoate were  79,77 and 89,66%, respectively. These compounds were well characterized by  spectroscopy techniques of infra red (IR), ultraviolet (UV), as well as based on  microelemental analyzer. The inhibition activity of triphenyltin(IV) 2-  hydroxibenzoate and triphenyltin(IV) 4-hydroxibenzoate on mild steel corrosion  in DMSO-HCl were studied with potentiodynamic polarization method. The  results showed that the triphenyltin(IV) 2-hydroxibenzoate and triphenyltin(IV) 4-  hydroxibenzoate act as good corrosion inhibitors for mild steel protection. The  high inhibition efficiency were attributed to the simple blocking effect by  adsorption of inhibitor molecules on the steel surface. The high percentage  efficiency inhibition (EI) values for the triphenyltin(IV) 2-hydroxibenzoate was  58,52 and triphenyltin(IV) 4-hydroxibenzoate was 61,72% at concentration of 100  ppm.  Keywords: triphenyltin(IV) hydroxibenzoate, potentiodynamic, corrosion.    
publisher: UNIVERSITAS LAMPUNG
date: 2016-04-27
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/22231/19/.ABSTRAK%20%28ABSTRACT%29.pdf
format: text
identifier: http://digilib.unila.ac.id/22231/20/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/22231/21/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   MURNI FITRIA, 1217011040  (2016) SINTESIS DAN KARAKTERISASI SENYAWA TRIFENILTIMAH(IV) HIDROKSIBENZOAT SEBAGAI INHIBITOR KOROSI PADA BAJA LUNAK DALAM DMSO-HCl.  UNIVERSITAS LAMPUNG, FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM .     
relation: http://digilib.unila.ac.id/22231/