title: PREPARASI DAN KARAKTERISASI LIMBAH BIOMATERIAL  CANGKANG KERANG KIJING (Pilsbryoconcha exilis) DARI  KECAMATAN PEKALONGAN SEBAGAI BAHAN DASAR  BIOKERAMIK
creator: HELRITA  MAULINA,  1017041029
subject: QC Physics
description: Telah dilakukan preparasi cangkang kerang kijing (Pilsbryoconcha exilis) dengan  tujuan untuk mengetahui pengaruh suhu kalsinasi terhadap gugus fungsional,  mikrostruktur, struktur kristal dan sifat termal bahan pembuatan biokeramik.  Cangkang kerang kijing yang digunakan diperoleh dengan mempreparasi sampel.  Cangkang kerang kijing yang telah dipreparasi kemudian dikalsinasi pada suhu  yang berbeda yaitu 500 °C, 800 °C dan 1000 °C, lalu dikarakterisasi. Analisis  dengan DTA/TG terjadi selisih penyusutan massa cangkang kerang dengan  kalsium karbonat komersil sebesar 0,03 %. Karakterisasi dengan FTIR  menunjukkan dalam sampel sebelum kalsinasi terdapat gugus fungsi O-H, C-H,  C-O dan CO3  2-. Setelah kalsinasi menunjukkan gugus fungsi O-H, C-H dan Ca-O.  Hasil analisis XRD menunjukkan sebelum kalsinasi memiliki fasa kalsium  karbonat fasa aragonite. Setelah kalsinasi kalsium karbonat terdekomposisi  menjadi kalsium oksida pada suhu 800 °C. Hasil karakterisasi menggunakan SEM  memperlihatkan hasil sampel memiliki struktur permukaan dan ukuran partikel  yang berbeda, yang sebelum kalsinasi dan setelah kalsinasi. Hasil karakterisasi  EDS menunjukkan bahwa kandungan terbesar yang terdapat pada sampel adalah  Ca.  Kata kunci: Cangkang kerang kijing (Pilsbryoconcha exilis), kalsinasi, kalsium  karbonat, kalsium oksida.    abstract    This preparation have been done for barnacle shells (Pilsbryoconchaexilis) with  the aim to determine the effect of calcination temperature on the functional  groups, microstructure, crystal structure and thermal of materials forbioceramic.  Barnacle shells which used for were obtained with doing a preparation samples.  Barnacle shells which have been prepared, itcalcined at some different  temperatures of 500 °C, 800 °C and 1000 °C, and then characterized. Analysis  sample by DTA / TG mass shrinkage difference occurs with calcium carbonate  shells commercial at 0.03%. Characterization by FTIR had shown in the sample  before calcination which are those functional groups O-H, C-H, C-O and CO3  2-.  Then, after calcination the sample showssome functional groups which are O-H,  C-H and Ca-O. The results of XRD analysis before calcination had an aragonite  phase of calcium carbonate. After calcination to decompose calcium carbonate  becomes calcium oxide at a temperature of 800 °C. The results of SEM  characterization has shownthat the samplehave a surface structure and some  different particle size, which before calcination and after calcination. The results  of EDS characterizationindicate that the largest content contained in the sample  is Ca.  Keywords: barnacle shells (Pilsbryoconchaexilis), calcining, calcium carbonate,  calcium oxide.
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM 
date: 2016-08-22
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/23663/1/ABSTRACT%20%28ABSTRAK%29.pdf
format: text
identifier: http://digilib.unila.ac.id/23663/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
format: text
identifier: http://digilib.unila.ac.id/23663/3/SKRIPSI%20FULL.pdf
identifier:   HELRITA MAULINA, 1017041029  (2016) PREPARASI DAN KARAKTERISASI LIMBAH BIOMATERIAL CANGKANG KERANG KIJING (Pilsbryoconcha exilis) DARI KECAMATAN PEKALONGAN SEBAGAI BAHAN DASAR BIOKERAMIK.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/23663/