N2  - Telah dilakukan penelitian mengenai efektivitas ekstrak daun sirsak sebagai
inhibitor pada baja karbon API 5L dalam larutan NaCl 3%. Perendaman baja
karbon API 5L dalam larutan NaCl 3% dilakukan selama 144 jam dengan variasi
konsentrasi penambahan inhibitor ekstrak daun sirsak 0%, 5%, 10%, 15%, 20%,
25%, 30%, dan 35%. Pengujian laju korosi dilakukan dengan metode kehilangan
berat dan metode elektrokimia. Hasil penelitian menunjukkan semakin besar
konsentrasi inhibitor ekstrak daun sirsak yang digunakan maka laju korosi akan
semakin berkurang dan kemampuan menginhibisi korosi akan meningkat.
Efektivitas korosi yang paling besar terjadi pada konsentrasi 35% pada
lingkungan NaCl 3% dengan efektivitas adalah 86,16%. Hasil karakterisasi X-Ray
Diffraction (XRD) memperlihatkan bahwa fasa yang terbentuk adalah Fe murni.
Karakterisasi Scanning Electron Microscopy (SEM) memperlihatkan cluster
(gumpulan) tidak merata dan ukuran lebih kecil, lubang (hole) dan retakan (crack)
juga lebih sedikit dengan inhibitor 35% dibandingkan dengan inhibitor 0% ekstrak
daun sirsak. Karakterisasi Energy Dispersive Spectroscopy (EDS) pada sampel
dengan inhibitor 0% didapatkan unsur Cl.
Kata kunci: Baja karbon API 5L, ekstrak daun sirsak, inhibitor korosi, dan NaCl.

ABSTRACT

The effectiveness of soursop leaves extract as inhibitor on carbon steel API 5L in
NaCl 3% had been researched. Carbon steel API 5L submersion used NaCl 3%
had been done for 144 hours with various concentrations of soursop leaves extract
inhibitor adding 0%, 5%, 10%, 15%, 20%, 25%, 30%, and 35%. The research of
corrosion rate was done by weight loss and electrochemistry methods. The result
showed that the higher percentage of soursop leaves extract inhibitor used, the
corrosion rate will decrease and capability of inhibit corrosion will increase. The
greatest effectiveness of corrosion occurred at concentration of 35% in NaCl 3%
and the effectiveness is 86,16%. The X-Ray Diffraction (XRD) characterization
result showed that the phase formed is pure Fe. Scanning Electron Microscopy
(SEM) characterization showed uneven clusters and smaller size, fewer holes and
cracks too with soursop leaves extract inhibitor 35% than soursop leaves extract
inhibitor 0%. Energy Dispersive Spectroscopy (EDS) characterization on sample
with inhibitor 0% obtained Cl element.
Key words: Carbon steel API 5L, corrosion inhibitor, NaCl and soursop leaves.
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - EFEKTIVITAS EKSTRAK DAUN SIRSAK SEBAGAI INHIBITOR PADA
BAJA KARBON API 5L DALAM LARUTAN NaCl 3%