N2  - Penelitian ini dilakukan untuk mengetahui pengaruh suhu kalsinasi terhadap
pembentukan fase zeolit, nilai konstanta standar kecepatan elektron (k0), dan
keterkaitan hubungan antara fase zeolit dengan nilai konstanta standar kecepatan
elektron (k0). Zeolit sintesis diperoleh dari pencampuran melalui reaksi kimia
menggunakan metode sol gel antara silika yang bersumber dari sekam padi dan
natrium alumina. Zeolit kemudian dikalsinasi pada suhu 150, 250, dan 350?C serta
dikarakterisasi menggunakan XRD (X-Ray Diffraction) dan CV (Cyclic
Voltammetry). Hasil analisis XRD pada suhu kalsinasi 150?C telah terbentuk fase
Gibbsite. Pada suhu kalsinasi 250?C telah terbentuk fase Gibbsite, Bohmite, dan
Quartz. Serta pada suhu kalsinasi 350?C terbentuk fase Bohmite dan Quartz. Hasil
analisis CV menunjukkan nilai k0 yang bervariasi, dan mekanisme reaksi yang
terjadi bersifat irreversible. Fase Gibbsite pada suhu kalsinasi 150?C diperoleh
nilai k0 tertinggi sebesar 3,75x10-7. Fase Gibbsite, Bohmite dan Quartz pada suhu
kalsinasi 250?C diperoleh nilai k0 tertinggi sebesar 1,52x10-7. Fase Bohmite dan
Quartz pada suhu kalsinasi 350?C diperoleh nilai k0 tertinggi sebesar 2,16x10-7.
Kata kunci: Elektrode, Zeolit, Elektrokimia, Reversibilitas, Superkapasitor.

ABSTRACT

This study was conducted to determine the effect of calcination on the zeolite
phase, the constant value standard velocity of the electron (k0), and the interrelationship
between the phase zeolite with constant value standard velocity
electron (k0). Synthetic zeolite obtained from mixing through a chemical reaction
using the silica sol gel derived from rice husk and sodium alumina. Zeolite then
calcined at a temperatures of 150, 250, and 350?C and characterized using XRD
(X-Ray Diffraction) and CV (Cyclic voltammetry). The results of XRD analysis
on the calcination 150?C Gibbsite phase has been formed, in the calcination 250?C
been formed Gibbsite, Bohmite, and Quartz. As well as the calcination 350?C
formed Bohmite phase and Quartz. CV analysis results showed the k0 value
varies, and the mechanism reaction is irreversible. Gibbsite phase at a calcination
150?C k0 highest values obtained by 3,75x10-7, Gibbsite phase, Bohmite and
Quartz on the calcination 250?C k0 highest values obtained by 1,52x10-7, as well
as the phase Bohmite and Quartz on the calcination values obtained 350?C k0
highest of 2,16x10-7.
Keywords: Electrodes, Zeolite, Electrochemistry, Reversibility, Supercapacitor.
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - PENGARUH SUHU KALSINASI (150, 250, DAN 350?C) PADA ELEKTRODE
SUPERKAPASITOR BERBAHAN ZEOLIT BERBASIS SILIKA SEKAM
PADI TERHADAP REVERSIBILITAS REAKSI ELEKTROKIMIA