title: PENGARUH VARIASI KUAT ARUS PENGELASAN TUNGSTEN
INERT GAS (TIG) TERHADAP KEKUATAN TARIK DAN
STRUKTUR MIKRO BAJA KARBON MEDIUM
ispublished: pub
subjects: TJ
full_text_status: restricted
abstract: ABSTRAK

Pengelasan Tungsten Inert Gas (TIG) adalah suatu proses pengelasan dengan
menggunakan gas mulia sebagai pelindung untuk mencegah terjadinya oksidasi
pada material pengelasan dengan udara luar. Untuk menghasilkan busur listrik,
digunakan elektroda yang tidak terkonsumsi terbuat dari logam tungsten atau
paduannya yang memiliki titik lebur sangat tinggi. Baja karbon medium
merupakan baja dengan kandungan karbon sebesar 0,36% dan merupakan
material yang cukup baik untuk digunakan dalam proses pengelasan. Penelitian ini
bertujuan untuk mengetahui kekuatan tarik hasil pengelasan tungsten inert gas
(TIG) pada baja karbon medium dengan menggunakan variasi kuat arus yang
berbeda. Dari hasil pengujian yang telah dilakukan, diketahui bahwa kekuatan
tarik tertinggi terdapat pada material hasil pengelasan 200 ampere dengan nilai
rata – rata kekuatan tarik sebesar 680 MPa. Sedangkan kekuatan tarik terendah
terdapat pada material hasil pengelasan 160 ampere dengan nilai rata – rata
kekuatan tarik sebesar 573,33 MPa. Hasil foto mikro menunjukan adanya
perbedaan antara logam dasar (raw material) dengan logam hasil pengelasan,
pada logam hasil pengelasan semakin kecil dan halus struktur mikronya
menghasilkan nilai kekuatan tarik yang semakin tinggi.
Kata kunci: Tungsten Inert Gas, Baja Karbon Medium, Kuat Arus, Kekuatan
Tarik, Struktur Mikro

ABSTRACT
Tungsten Inert Gas welding (TIG) is a welding process of using the noble gases as
protector to prevent the occurrence of oxidation on the welding material with
outside air. For generating an electric arc, by using the electrode is not consumed
tungsten metal made or its alloys which have a very high melting point. Medium
carbon steel is carbon steel with carbon content of 0.36% and these is a pretty
good material for use in welding processes. This research aims to know the results
of the tensile strength of welding Tungsten Inert Gas (TIG) on Medium carbon
steel by using different current variations. The results of testing that has been
done, it is known that the highest tensile strength of material contained on the
welding results of 200 ampere with value average tensile strength of 680 MPa.
While the lowest tensile strength of the material contained on the welding results
of 160 ampere with value average tensile strength of 573,33 MPa. The results
showed the existence of micro-photograph of the differences between the base
metals (raw material) with weld metal, the result of welding metal is getting
smaller and delicate of microstructure that produce the higher value of the tensile
strength.
Keywords: Tungsten Inert Gas, Medium Carbon Steel, Current Strength, Tensile
Strength, Microstructure
date: 2016-11-03
publisher: FAKULTAS TEKNIK
place_of_pub: UNIVERSITAS LAMPUNG
citation:   GALIH PAMUNGKAS , 1015021032  (2016) PENGARUH VARIASI KUAT ARUS PENGELASAN TUNGSTEN INERT GAS (TIG) TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO BAJA KARBON MEDIUM.  FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/24654/1/ABSTRAK%20%28ABSTRACT%29.pdf
document_url: http://digilib.unila.ac.id/24654/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/24654/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf