title: PENGARUH UKURAN SERBUK ABU TERBANG BATUBARA TERHADAP  LAJU KEAUSAN KOMPOSIT ABU TERBANG BATUBARA / PHENOLIC
creator: MUHAMMAD FATHLIANSYAH P, 1115021055
subject: Teknik mesin dan mesin
description: Kebutuhan akan material kuat, murah, dan ringan semakin meningkat kian waktu,  komposit dapat menjadi sebuah solusi akan kebutuhan tersebut dimana bahan  penyusun komposit ada yang berasal dari alam dan limbah hasil industri.  Pemanfaatan abu terbang batubara juga dapat digunakan dalam pembuatan komposit.  Pada penelitian ini dilakukan pembuatan komposit abu terbang batubara/phenolic  dengan menggunakan variasi ukuran serbuk pada proses hot pressing. Sehingga dapat  diketahui pengaruh variasi ukuran serbuk abu terbang batubara terhadap laju keausan  komposit abu terbang batubara/phenolic.  Penelitian ini dilakukan dengan variasi serbuk abu terbang batubara 100 mesh, 150  mesh, dan 200 mesh. Komposit abu terbang batubara/phenolic memiliki bahan  penyusun dengan komposisi matrik phenolic 60%, sebagai penguat abu terbang batubara,  grafit, serbuk besi 20%, barium sulfat 10% sebagai pengisi, dan Nitril Butadiene Rubber  10% sebagai pengikat, diproses dengan metode hot pressing, temperatur pemanasan yang  digunakan 250oC, tekanan 60 Mpa, dan temperatur curing 150oC.  Ukuran serbuk abu terbang batubara 200 mesh memiliki ketahanan aus terbaik pada  penelitian ini, yang membuktikan bahwa ukuran serbuk berpengaruh terhadap sifat  mekanik suatu material, kecilnya ukuran serbuk abu terbang batubara inilah yang  membuatnya dapat tersebar dan terikat dengan baik pada bahan lain dan mengisi  rongga pada komposit. Pada pengujian keausan komposit abu terbang batubara  diperoleh nilai spesifik abrasi yang diambil nilai rata-rata, komposit pada ukuran  serbuk abu terbang batubara 100 mesh diperoleh hasil spesifik abrasi sebesar  14,589×10-6mm3/mm, pada ukuran serbuk abu terbang batubara 150 mesh diperoleh  hasil spesifik abrasi sebesar 19,987×10-6 mm3/mm, pada ukuran serbuk abu terbang  batubara 200 mesh diperoleh hasil spesifik abrasi sebesar 12,782×10-6mm3/mm.  Kata kunci : Komposit Abu terbang Batubara/Phenolic, Hot Pressing, keausan    ABSTRACT    The need for strong material, inexpensive, and lightweight growing increasingly time,  and the composite can be a solution to these needs, which the constituents of the  composite were from natural and industrial wastes. Utilization of coal fly ash can also  be used in the manufacture of composites. This research is manufacture of composite  coal fly ash/phenolic powder size by using a variation on the process of hot pressing.  The effect of variations in the size of powder coal fly ash on composite wear rate of  coal fly ash/phenolic can be seen.  This research was conducted with the variation of coal fly ash powder of 100 mesh,  150 mesh, and 200 mesh. Composite coal fly ash/phenolic has the constituents of the  composition of the matrix of phenolic 60%, as the reinforcement of fly ash coal,  graphite, iron powder 20%, barium sulfate 10% as a filler, and nitrile butadiene  rubber 10% as a binder, is processed by method of hot pressing, the heating  temperature is used to 250oC, a pressure of 60 MPa and temperature of 150oC curing.  Powder size of fly ash coal 200 mesh has wear resistance best in this research which  proves that the size of the powder affect the mechanical properties of a material. The  small size of the powder coal fly ash is what makes it distributed evenly and adherent  to the other ingredients. In testing the wear of coal fly ash composite obtained  specific values taken abrasion average value, composite powder size of 100 mesh  coal fly ash obtained specific results of abrasion of 14,589×10-6mm3/mm, the powder  size of 150 mesh coal fly ash obtained specific results of abrasion of 19,987×10-6  mm3/mm, the size of the coal fly ash powder of 200 mesh obtained specific results of  abrasion of 12,782×10-6mm3/mm.  Keywords: Composite Coal Fly Ash/Phenolic, Hot Pressing, Wearing
publisher: FAKULTAS TEKNIK
date: 2016-11-30
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/24687/1/ABSTRACT%20%28ABSTRAK%29.pdf
format: text
identifier: http://digilib.unila.ac.id/24687/2/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/24687/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   MUHAMMAD FATHLIANSYAH P, 1115021055  (2016) PENGARUH UKURAN SERBUK ABU TERBANG BATUBARA TERHADAP LAJU KEAUSAN KOMPOSIT ABU TERBANG BATUBARA / PHENOLIC.  FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/24687/