title: SINTESIS DAN KARAKTERISASI NANOTITANIA YANG DIDOPING
FLUOR MENGGUNAKAN METODE SOL-GEL
ispublished: pub
subjects: QC
full_text_status: restricted
abstract: Telah dilakukan sintesis dan karakterisasi nanotitania menggunakan metode solgel.
Sebagai sumber titania digunakan titanium tetraisopropoxide (TTIP) dan
isoprophyl alcohol sebagai pelarut. Dalam mensintesis digunakan tween-80
sebagai surfaktan dan NH4F sebagai sumber doping fluor (F). Jumlah sampel yang
disintesis sebanyak satu sampel nanotitania murni dan empat sampel F-TiO2
dengan variasi doping F masing-masing 0,4 g; 0,6 g; 0,8 g dan 1 g. Sampel
dikalsinasi pada suhu 500 ℃ selama 4 jam. Seluruh sampel berbentuk bubuk dan
dikarakterisasi menggunakan X-Ray Diffraction (XRD), Transmission Electron
Microscope (TEM), Ultra Violet Visible (UV-Vis) Spectroscopy dan uji aktivitas
katalitik pada larutan fenol 100 ppm. Hasil uji XRD menunjukkan bahwa sampel
nanotitania dan F-TiO2 memiliki fasa murni anatase dengan ukuran partikel
masing-masing sebesar 16,8 nm dan 23,8 nm. Penambahan doping F dipandang
dapat meningkatkan kristalinitas nanotitania. Hasil uji TEM didapatkan ukuran
partikel nanotitania 22,6 nm dan 21,1 nm untuk F-TiO2. Hasil uji aktivitas katalis
menunjukkan bahwa dengan penambahan doping F pada nanotitania
mengakibatkan kemampuan fotokatalitik nanotitania mengalami peningkatan di
bawah sinar matahari (visible light).
Kata kunci: Fenol, metode sol-gel, NH4F, titania, uji aktivitas katalis.

ABSTRACT

The synthesis and characterization of nanotitania has been carried out by sol-gel
method. Titanium tetraisopropoxide (TTIP) used as a source of titania and
isoprophyl alcohol as a solvent. In the synthesis, tween-80 was added as a
surfactant and as a source of fluor (F) doping was used NH4F with variation of
0,4; 0,6; 0,8 and 1 gram. Samples were calcined at 500 ℃ for 4 hours. The whole
sample were characterized using X-Ray Diffraction (XRD), Transmission
Electron Microscope (TEM), Ultra Violet Visible (UV-Vis) spectroscopy and test
catalytic activity at 100 ppm phenol solution. XRD test results showed that the
samples nanotitania and F- TiO2 has a pure anatase phase with particle sizes of
16.8 nm and 23.8 nm. The addition of F doping can improve the crystallinity of
nanotitania. TEM results showed that particle size of 22.6 nm for nanotitania and
21.1 nm for F-TiO2. The results of the catalyst activity test showed that the
addition of F doping on nanotitania enhanced photocatalytic ability of nanotitania
in sunlight (visible light).
Keywords: Catalyst activity test, NH4F, phenol, sol-gel method, titania.
date: 2017-01-20
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM 
place_of_pub: UNIVERSITAS LAMPUNG
institution: UNIVERSITAS LAMPUNG
department: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
thesis_type: masters
citation:    LAURA MEGADIA SARI, (1427041004)  (2017) SINTESIS DAN KARAKTERISASI NANOTITANIA YANG DIDOPING FLUOR MENGGUNAKAN METODE SOL-GEL.  Masters thesis, UNIVERSITAS LAMPUNG.   
document_url: http://digilib.unila.ac.id/25360/1/ABSTRAK%20%28ABSTRACT%29.pdf
document_url: http://digilib.unila.ac.id/25360/2/TESIS%20FULL.pdf
document_url: http://digilib.unila.ac.id/25360/3/TESIS%20TANPA%20BAB%20PEMBAHASAN.pdf