abstract: ABSTRAK

Pada penelitian ini, zeolit sintetik telah disintesis dari silika sekam padi dan logam
aluminium menggunakan metode elektrokimia pada potensial tetap 6 volt dan
variasi waktu elektrolisis selama 1, 2, dan 3 jam. Zeolit yang dihasilkan secara
spesifik dikenal dengan Zeo(6:1), yakni yang dihasilkan dengan waktu 1 jam,
Zeo(6:2) untuk zeolit yang dihasilkan dari percobaan 2 jam, dan Zeo(6:3) untuk
zeolit yang dihasilkan dari percobaan 3 jam. Zeolit tersebut kemudian dikalsinasi
pada suhu 600, 700, 800, dan 900°C dan digunakan dalam proses transesterifikasi
minyak kelapa, minyak kelapa sawit, dan minyak jarak pagar. Hasil percobaan
menunjukkan bahwa semua katalis memiliki aktivitas katalitik. Untuk minyak
kelapa sawit, persen konversi tertinggi (80%) diperoleh dari percobaan
menggunakan Zeo(6:2) yang dikalsinasi pada suhu 900°C, sedangkan untuk minyak
jarak pagar, katalis terbaik dengan persen konversi sebesar 82% adalah Zeo(6:2)
yang dikalsinasi pada suhu 600°C. Data XRD menunjukkan bahwa Zeo(6:2) terdiri
atas fasa albite, nepheline, dan stilbite-Na. Dengan nisbah Si/Al sebesar 3,312,
Zeo(6:2) tergolong ke dalam zeolit sintetik bersilika sedang. Hasil SEM
menggambarkan katalis Zeo(6:2) suhu kalsinasi 600 dan 700°C lebih bersifat amorf
dengan distribusi ukuran partikel 18,17 – 58,77 dan 122,4 – 342 nm, sedangkan
pada suhu 800 dan 900°C bersifat kristalin dengan distribusi ukuran partikel 220,2
– 712,4 nm. Spektrum FTIR menunjukkan bahwa katalis Zeo(6:2) mengandung
jenis situs asam Brønsted-Lowry.
Kata kunci : zeolit sintetik, elektrokimia, transesterifikasi, biodiesel,
Brønsted-Lowry

ABSTRACT

In this study, synthetic zeolites have been produced from rice husk silica and
aluminum by using electrochemical method performed at specified potential of 6
V and varied electrolysis times of 1, 2, and 3 hours. The zeolites produced are
specified as zeolite 6 V, 1 hour (Zeo(6:1)), 6 V, 2 hours (Zeo(6:2)) and 6 V, 3 hours
(Zeo(6:3)). The zeolites were calcined at 600, 700, 800, and 900°C, then applied in
transesterification of coconut oil, palm oil and jatropha oil. The experimental
results demonstrated that all catalysts exhibited catalytic activity. For palm oil,
the highest conversion (80%) is achieved with Zeo(6: 2) calcined at 900°C, while
for jatropha oil, the best catalyst with the conversion of 82% is Zeo(6: 2) with
calcination temperature at 600°C. The XRD results show that Zeo(6:2) is
composed of albite, nepheline and stilbite-Na phases. With Si/Al ratio of 3.312,
Zeo(6:2) belongs to synthetic zeolite with intermediate silica content. The SEM
micrographs indicate that Zeo(6:2) calcined at 600 and 700°C are more amorphous
with particle size distribution of 18.17 - 58.77 and 122.4 - 342 nm, whereas at 800
and 900°C Zeo(6:2) are crystalline with particle size distribution of 220.2 - 712.4
nm. The FTIR spectrums show that Zeo(6:2) contain Brønsted-Lowry acid site.
Keyword: synthetic zeolite, electrochemical, transesterification, biodiesel,
Brønsted-Lowry
date: 2017-07-31
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
place_of_pub: UNIVERSITAS LAMPUNG
citation:   GESA GUSTAMI PANGESTI, 1317011028  (2017) PENGOLAHAN MINYAK KELAPA SAWIT DAN MINYAK JARAK PAGAR MENJADI BIODIESEL MENGGUNAKAN ZEOLIT SINTETIK BERBASIS SILIKA SEKAM PADI SEBAGAI KATALIS.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/27853/1/ABSTRAK%20%28ABSTRACT%29.pdf
document_url: http://digilib.unila.ac.id/27853/3/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/27853/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf