?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=KONVERSI+NANOSELULOSA+MENJADI+GULA+ALKOHOL+DENGAN+MENGGUNAKAN+NANOFOTOKATALIS+LaCr0%2C99Mo0%2C01O3+YANG+DIIRADIASI+SINAR+ULTRAVIOLET&rft.creator=Esti+Sandra+Pertiwi%2C+1347011001&rft.subject=+&rft.subject=QD+Chemistry&rft.description=Telah+dilakukan+preparasi+nanokatalis+LaCr0%2C99Mo0%2C01O3+dengan+metode+sol+gel+dan+pelarut+pektin+pada+suhu+kalsinasi+700+oC+serta+uji+aktivitas+katalitiknya+dalam+konversi+nanoselulosa+menjadi+gula+alkohol.++Karakterisasi+katalis+meliputi+analisis+keasaman%2C+analisis+morfologi+katalis+(TEM)+dan+analisis+fasa+kristalin+(XRD).+Selanjutnya%2C+hasil+uji+katalitik+konversi+nanoselulosa+dianalisis+menggunakan+KCKT.+Hasil+analisis+keasaman+katalis+LaCr0%2C99Mo0%2C01O3+yang+dikalsinasi+pada+suhu+700+oC+sebesar+13%2C85+mmol+piridin%2Fgram+katalis+dengan+jenis+situs+asam+yaitu+situs+asam+Bronsted-Lowry.+Hasil+analisis+morfologi+katalis+menunjukkan+masih+banyak+terjadi+aglomerisasi+dan+diperoleh+ukuran+rata-rata+partikel+dari+tiga+spot+pada+katalis+LaCr0%2C99Mo0%2C01O3+sebesar+38%2C67+nm.+Analisis+XRD+dari+katalis+yang+dikalsinasi+pada+suhu+700+oC+membentuk+fasa+kristalin+La2Mo2O9+dan+LaCrO3+dengan+ukuran+rata-rata+partikel+yang+dihasilkan+dari+persamaan+Scherrer+sebesar+47%2C77+nm.+Analisis+menggunakan+KCKT+mengungkapkan+bahwa+nanoselulosa+dikonversi+menjadi+sorbitol+dengan+konsentrasi+tertinggi+sebesar+19%2C07+%25+yang+dihasilkan+dari+lama+penyinaran+45+menit.%0D%0A%0D%0AKata+kunci%3A+nanoselulosa%2C+gula+alkohol%2C+pektin.%0D%0A%0D%0A%0D%0A%0D%0Aabstract%0D%0A%0D%0ALaCr0.99Mo0.01O3+nanocatalyst+was+prepared+by+sol+gel+method+and+pectin+as+an+emulsifying++agent+after+freeze+drying+and+calcinating+at+700+oC%2C+the+catalyst+was+used+to+convert+nanocellulose+into+alcohol+sugar.++Characterization+was+the+calcined+sample+was+characterized+with+several+techiques%2C+such+as+XRD%2C+FTIR%2C+and+TEM.++The+XRD+analysis+indicated+that+sample+consists+of++both+La2Mo2O9+and+LaCrO3+as+a+major++phase+with+the+average+crystallite+size+of++47.77+nm+using+Scherrer+calculation.++FTIR+analysis+revealed+the+existence+of+Bronsted-Lowry+acid+sites+as+presented+by+1620.21+cm-1.++The+morphology+analysis+using+TEM+that+there+is+still+aglomerization+and+%09grain+size+is+38.67+nm.++The+results+of+nanocellulose+conversion+into+sorbitol+is+analyzed+by+HPLC+with+19.07%25+of+yield.%0D%0A%0D%0AKeywords+%3A+Nanocellulose%2C+alcoholsugar%2C+pectin%0D%0A%0D%0A&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+&rft.date=2017-10-04&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F28774%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F28774%2F9%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F28774%2F10%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++Esti+Sandra+Pertiwi%2C+1347011001++(2017)+KONVERSI+NANOSELULOSA+MENJADI+GULA+ALKOHOL+DENGAN+MENGGUNAKAN+NANOFOTOKATALIS+LaCr0%2C99Mo0%2C01O3+YANG+DIIRADIASI+SINAR+ULTRAVIOLET.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F28774%2F