%0 Generic
%A MARIO SALIMOR , 1015021066
%C UNIVERSITAS LAMPUNG
%D 2017
%F eprints:29618
%I FAKULTAS TEKNIK
%T SIFAT TERMOMEKANIKAL DAN KETANGGUHAN BAJA AISI 1018  PADA SUHU TINGGI
%U http://digilib.unila.ac.id/29618/
%X Sifat mekanik baja tarik dingin (CDS) AISI 1018 diuji tarik pada suhu 25 °C sampai  750 °C pada kondisi steady state (keadaan tunak). Penurunan sifat mekanik CDS  pada suhu yang berbeda ditunjukkan pada faktor reduksi modulus elastis, kekuatan  luluh, dan kekuatan tertinggi. Selain itu, setelah pengujian mekanik, mikrostruktur  baja di daerah fraktur (patahan) diuji menggunakan mikroskop elektron (SEM) dan  pada permukaan spesimen baja diamati dengan mikroskop optik (OM). Berdasarkan  standar desain yang ada saat ini, perbandingan faktor reduksi diusulkan untuk  penerapan CDS pada suhu tinggi. Hasilnya menunjukkan bahwa hubungan  pengamatan (empiris) yang direkomendasikan oleh standar saat ini tidak dapat  digunakan untuk memprediksi sifat mekanik CDS. Dalam suatu sisi produk baja, baja  cold-formed (CFS) atau high-strength steel (HSS) menunjukkan faktor reduksi yang  berbeda dari CDS pada suhu tinggi. Oleh karena itu, pengamatan untuk faktor reduksi  diusulkan dalam kisaran suhu dari 100 °C sampai 750 °C. DSA disebabkan  pengerasan yang bekerja pada CDS termasuk dalam peraturan kode rasional  berdasarkan pengaplikasian material pada desain suhu tinggi.  Kata kunci : baja tarik dingin, peralatan mekanis, faktor reduksi, pengerasan yang  bekerja, desain suhu tinggi.    ABSTRACT      The mechanical properties of cold-drawn steel (CDS) AISI 1018 were measured  experimentally in the temperature range of 25 °C to 750 °C under steady-state  conditions. The deterioration of the mechanical properties of the CDS at different  temperatures was represented in terms of the reduction factors of the elastic modulus,  yield strength, and ultimate strength. In addition, after mechanical testing, the steel  microstructures at the fracture region were examined by scanning electron  microscopy (SEM), and the fractographs of the surface of the steel specimens were  observed by optical microscopy (OM). Based on the available current design  standards, comparisons of the reduction factor were proposed for application of CDS  at elevated temperatures. The results show that the empirical relations recommended  by the current standards cannot be used to predict the mechanical properties of CDS.  In the side view of steel products, either cold-formed steel (CFS) or high-strength  steel (HSS) showed a different reduction factor than the CDS at elevated  temperatures. Therefore, predictive equations for the reduction factors were proposed  in the temperature range from 100 °C to 750 °C. Dynamic strain aging induced work  hardening of CDS is included in the prescriptive code rules for rational hightemperature  material application based design.  Keywords : cold-drawn steel; mechanical properties; reduction factor; work  hardening; high-temperature design