?url_ver=Z39.88-2004&rft_id=1315021053&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+MEDIA+AIR+YANG+TERSIRKULASI+PADA+PROSES+QUENCHING+TERHADAP+KEKERASAN+DAN+STRUKUR+MIKRO+BAJA+AISI+1045&rft.creator=RAHMAD+SATRIA+WIJAYA%2C+1315021053&rft.subject=Mesin+(General).+Mesin+Sipil+(General)&rft.description=Penelitian+proses+pengaruh+media+air+yang+tersirkulasi+pada+proses+quenching+terhadap+kekerasan+dan+struktur+mikro+baja+AISI+1045+bertujuan+untuk+mengetahui+sifat+mekanis+yakni+nilai+kekerasan+dan+struktur+mikro+dari+baja.+Baja+AISI+1045+diberi+perlakuan+panas+dengan+suhu+850%CB%9AC+selama+20+menit%2C+diquenching+dengan+media+air+yang+tersirkulasi.+Variasi+kecepatan+air+yang+tersirkulasi+pada+media+air+dengan+laju+aliran+Q1+(V%3D0+m%2Fs)%2C+laju+aliran+Q2+(V%3D+0%2C77381m%2Fs)%2C+laju+aliran+Q3(V%3D0%2C95238m%2Fs)%2C+dan+laju+aliran+Q4+(V%3D1%2C07143m%2Fs).+Proses+uji+kekerasan+yang+menghasilkan+nilai+kekerasan+Q0+yakni+normalizing+yang+menghasilkan+nilai+rata-rata+59%2C33+HRB+%2C+pada+Q1+yakni+proses+quencing+tanpa+agitasi+menghasikan+nilai+rata-rata+78%2C33+HRB%2C+pada+Q2+yakni+proses+quencing+agitasi+dengan+bukaan+katup+%C2%BC+menghasilkan+nilai+rata-rata+82%2C89+HRB%2C+pada+Q3+yakni+proses+quenching+agitasi+dengan+bukaan+katup+%C2%BD+menghasilkan+nilai+rata-rata+87%2C11+HRB%2C+dan+Q4+yakni+proses+quenching+agitasi+dengan+bukaan+katup+1+(penuh)+menghasilkan+nilai+rata-rata+95%2C11+HRB.+Proses+quenching+pada+Baja+AISI+1045+dengan+metode+air+tersirkulasi+menghasilkan+struktur+martensite+pada+pengujian+analisis+struktur+mikro.%0D%0A%0D%0AKata+kunci+%3A+Baja+AISI+1045%2C+Quenching%2C+Kekerasan%2C+Struktur+Mikro.+%0D%0A%0D%0AABSTACT%0D%0A%0D%0A%0D%0AResearch+on+the+effect+of+circulating+water+media+on+the+quenching+process+on+hardness+and+microstructure+of+steel+AISI+1045+aims+to+know+the+mechanical+properties+of+hardness+value+and+micro+structure+of+steel.+The+AISI+1045+steel+arm+was+treated+with+a+temperature+of+850%CB%9AC+for+20+minutes%2C+then+quenching+with+a+circulating+water+medium.+Subsequently%2C+variations+of+water+velocity+are+circulated+in+water+medium+with+flow+rate+Q1+(V+%3D+0+m+%2F+s)%2C+flow+rate+Q2+(V+%3D+0.77381m+%2F+s)%2C+flow+rate+Q3+(V+%3D+0.95238+m+%2F+s)%2C+and+flow+rate+Q4+(V+%3D+1%2C07143m+%2F+s).+After+that+is+done+process+of+hardness+test+that+yield+hardness+value+of+Q0+that+is+normalizing+which+yield+average+value+59%2C33+HRB%2C+then+Q1+ie+quitting+process+without+agitation+resulted+average+value+78%2C33+HRB%2C+at+Q2+ie+process+of+agencing+agitation+with+valve+opening+%C2%BC+yields+an+average+value+of+82.89+HRB%2C+in+Q3+the+quenching+process+of+agitation+with+%C2%BD+valve+opening+yields+an+average+value+of+87.11+HRB%2C+and+then+Q4+ie+agitation+quenching+process+with+1+(full)+valve+opening+yields+an+average+value+95.11+HRB.+While+quenching+process+on+AISI+1045+Steel+with+circulated+water+method+can+produce+martensite+structure+in+micro+structure+analysis+test.%0D%0A%0D%0AKeywords%3A+AISI+1045+Steel%2C+Quenching%2C+Hardness%2C+Micro+Structure.%0D%0A&rft.publisher=FAKULTAS+TEKNIK&rft.date=2018-02-19&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F30738%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F30738%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F30738%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++RAHMAD+SATRIA+WIJAYA%2C+1315021053++(2018)+PENGARUH+MEDIA+AIR+YANG+TERSIRKULASI+PADA+PROSES+QUENCHING+TERHADAP+KEKERASAN+DAN+STRUKUR+MIKRO+BAJA+AISI+1045.++FAKULTAS+TEKNIK%2C++UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F30738%2F