title: ANALISIS PERAMBATAN RETAK FATIK PADA STAINLESS STEEL 304  YANG DILAPISI ALUMINIUM CELUP PANAS
creator: FARID NANDA SYANUR , 1215021037
subject: Teknik mesin dan mesin
description: Stainless steel merupakan baja paduan tinggi yang memiliki ketangguhan pada  temperatur rendah maupun tinggi serta sifat ketahanan korosi yang baik. Stainless  steel yang digunakan yaitu stainless steel 304. Stainless steel 304 dilapisi aluminium  celup panas untuk meningkatkan kemampuan mekaniknya. Stainless steel 304 diberi  perlakuan difusi pada suhu 750o C dengan waktu tahan 1 sampai 49 jam. Perlakuan  difusi dapat menurunkan kekuatan mekanik pada stainless steel 304. Stainless steel  304 mengalami penurunan nilai tegangan luluh (18,89%) dan nilai tegangan  maksimum (11,73%.). Nilai tegangan luluh dan nilai tegangan maksimum terendah  yaitu 285,360 MPa dan 540,325 MPa. Laju perambatan retak fatik Stainless steel 304  tanpa perlakuan memiliki jumlah siklus terbesar serta ketahanan fatik yang lebih baik  dibandingkan dengan stainless steel 304 lapis aluminium celup panas dengan  perlakuan difusi yang memiliki jumlah siklus lebih pendek dan laju perambatan retak  yang cepat. Berdasarkan nilai laju perambatan retak fatik stainless steel 304 bahwa  tidak semua dengan proses pelapisan dapat meningkatkan kekuatan mekanik pada  material. Karakterisasi dari uji SEM (Scanning Electron Microscope) stainless steel  304 lapis Aluminium dengan diffusion treatment mengalami patahan yang lebih getas  dibandingkan dengan stainless steel 304 tanpa perlakuan (base metal).  Kata kunci: Stainless steel, Aluminium Celup Panas, Difusi, Perambatan Retak  Fatik, SEM (Scanning Electron Microscope).    abstract    Stainless steel is a high alloy steel that has a toughness at low or high temperatures  and good corrosion resistance properties. Stainless steel used is stainless steel 304.  Stainless steel 304 coated aluminum hot dip to improve mechanical ability. Stainless  steel 304 is given diffusion treatment at 750° C with a holding time of 1 to 49 hours.  The diffusion treatment can decrease the mechanical strength of stainless steel 304.  Stainless steel 304 has decreased yield strength (18.89%) and ultimate tensile strength  value (11.73%.). The lowest value of yield strength and ultimate tensile strength is  285.360 MPa and 540.325 MPa. Fatigue crack propagation rate stainless steel 304  without treatment has the greatest number of cycles as well as better fatigue  resistance compared to stainless steel 304 layers of hot dipped aluminum with  diffusion treatment having shorter cycle counts and more fast crack propagation  growth. Based on the rate of fatigue crack propagation of stainless steel 304 that not  all materials with coating process can increase their mechanical strength.  Characterization from SEM (Scanning Electron Microscope) experience of stainless  steel 304 Aluminum-coated with diffusion treatment had a more brittle fracture  compared to stainless steel 304 without treatment (base metal).  Keywords: Stainless steel, Hot Dip Aluminizing Coating, Diffusion Treatment,  Fatigue Crack Propagation, SEM (Scanning Electron Microscope).
publisher: FAKULTAS TEKNIK 
date: 2018-04-05
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/31068/1/ABSTARCT%20%28ABSTRAK%29.pdf
format: text
identifier: http://digilib.unila.ac.id/31068/2/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/31068/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   FARID NANDA SYANUR , 1215021037  (2018) ANALISIS PERAMBATAN RETAK FATIK PADA STAINLESS STEEL 304 YANG DILAPISI ALUMINIUM CELUP PANAS.  FAKULTAS TEKNIK , UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/31068/